- 弯曲模量 [MPa]: 9.6138
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.63 g/cc | 1.63 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.00 cm/cm | 0.00 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 127.53 MPa | 18497 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 127.53 MPa | 18497 psi | ASTM D790 |
| Flexural Modulus | 9.6138 GPa | 1394.4 ksi | ASTM D790 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ASTM D257 |
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz | 3.2 @Frequency 1.00e+6 Hz | ASTM D150 |
| Dielectric Strength | 26.0 kV/mm @Thickness 1.60 mm | 660 kV/in @Thickness 0.0630 in | ASTM D149 |
| Dissipation Factor | 0.028 @Frequency 1.00e+6 Hz | 0.028 @Frequency 1.00e+6 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 8.00 µm/m-°C @Thickness 1.60 mm | 4.44 µin/in-°F @Thickness 0.0630 in | ASTM D696 |
| CTE, linear, Transverse to Flow | 22.0 µm/m-°C @Thickness 1.60 mm | 12.2 µin/in-°F @Thickness 0.0630 in | ASTM D696 |
| Melting Point | 335 °C | 635 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 239 °C | 462 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 350 - 360 °C | 662 - 680 °F | |
| Mold Temperature | 30.0 - 150 °C | 86.0 - 302 °F | |