- 密度 [g/cm3]: 1.61
- 缺口冲击强度: 20.0
- 弯曲模量 [MPa]: 13.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.61 g/cc | 0.0582 lb/in³ | ISO 1183 | ||
| Moisture Absorption | 0.0300 % | 0.0300 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.00100 cm/cm | 0.00100 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.00500 cm/cm | 0.00500 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 71.0 | 71.0 | ISO 2039-2 | ||
| Tensile Strength at Break | 150 MPa | 21800 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 1.60 % | 1.60 % | 5mm/min; ISO 527-2/1A | ||
| 2.20 % | 2.20 % | Flexural strain; ISO 178 | |||
| Tensile Modulus | 15.0 GPa | 2180 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 220 MPa | 31900 psi | ISO 178 | ||
| Flexural Modulus | 13.5 GPa | 1960 ksi | ISO 178 | ||
| Compressive Strength | 93.0 MPa | 13500 psi | 1% strain; ISO 604 | ||
| Compressive Modulus | 14.0 GPa | 2030 ksi | ISO 604 | ||
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | ISO 180/1A | ||
| Izod Impact, Unnotched (ISO) | 31.0 kJ/m² | 14.8 ft-lb/in² | ISO 180/1U | ||
| Charpy Impact Unnotched | 4.30 J/cm² | 20.5 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 2.20 J/cm² | 10.5 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | ||
| Dielectric Constant | 3.30 @Frequency 1.00e+6 Hz | 3.30 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 4.00 @Frequency 100 Hz | 4.00 @Frequency 100 Hz | IEC 60250 | |||
| 4.23 @Frequency 2.05e+9 Hz | 4.23 @Frequency 2.05e+9 Hz | IPC TM-650 2.5.5.13 | |||
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.00600 @Frequency 2.05e+9 Hz | 0.00600 @Frequency 2.05e+9 Hz | IPC TM-650 2.5.5.13 | ||
| 0.0100 @Frequency 100 Hz | 0.0100 @Frequency 100 Hz | IEC 60250 | |||
| 0.0250 @Frequency 1.00e+6 Hz | 0.0250 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Arc Resistance | 140 sec | 140 sec | Internal | ||
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 7.00 µm/m-°C | 3.89 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 335 °C | 635 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 276 °C | 529 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 8.0 MPa | 216 °C | 421 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 195 °C | 383 °F | B50 (50°C/h 50N); ISO 306 | ||
| Flammability, UL94 | V-0 | V-0 | UL94 | ||
| Oxygen Index | 45.0 % | 45.0 % | ISO 4589 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 30.0 °C | 68.0 - 86.0 °F | |||
| 80.0 - 120 °C | 176 - 248 °F | Cavity temperature | |||
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Zone 1 | 315 - 325 °C | 599 - 617 °F | |||
| Zone 2 | 320 - 330 °C | 608 - 626 °F | |||
| Zone 3 | 325 - 335 °C | 617 - 635 °F | |||
| Zone 4 | 330 - 340 °C | 626 - 644 °F | |||
| Die Temperature | 335 - 345 °C | 635 - 653 °F | |||
| Melt Temperature | 335 - 345 °C | 635 - 653 °F | |||
| 340 °C | 644 °F | Injection molding; ISO 294 | |||
| Mold Temperature | 100 °C | 212 °F | Injection molding; ISO 294 | ||
| Injection Velocity | 150 mm/sec | 5.91 in/sec | ISO 294 | ||
| Drying Temperature | 150 - 170 °C | 302 - 338 °F | |||
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |||
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual | ||
| Dew Point | <= -40.0 °C | <= -40.0 °F | Pre-drying | ||
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| Hold Pressure | 69.0 MPa | 10000 psi | ISO 294 | ||
| 50.0 - 150 MPa | 7250 - 21800 psi | ||||
| Back Pressure | 3.00 MPa | 435 psi | |||
| Screw Speed | 80.0 rpm @Diameter 40.0 mm | 80.0 rpm @Diameter 1.57 in | |||
| 140 rpm @Diameter 25.0 mm | 140 rpm @Diameter 0.984 in | ||||
| 200 rpm @Diameter 16.0 mm | 200 rpm @Diameter 0.630 in | ||||
| Hot-Working Temperature | 335 - 345 °C | 635 - 653 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | very fast | ||||
| Longer pre-drying times/storage | 100° C. | <= 60 h | |||
| Short metering strokes | accumulator is recommended | to get short injection times | |||