- 密度 [g/cm3]: 1.46
- 缺口冲击强度: 40.0
- 弯曲模量 [MPa]: 14.0
- 热变形温度 [℃]: 298.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | -0.00200 cm/cm | -0.00200 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.00500 cm/cm | 0.00500 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 43.0 | 43.0 | ISO 2039-2 | ||
| Tensile Strength at Break | 175 MPa | 25400 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 2.30 % | 2.30 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 14.0 GPa | 2030 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 210 MPa | 30500 psi | ISO 178 | ||
| Flexural Modulus | 14.0 GPa | 2030 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | ISO 180/1A | ||
| Izod Impact, Unnotched (ISO) | 101 kJ/m² | 48.1 ft-lb/in² | ISO 180/1U | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.94 @Frequency 2.05e+9 Hz | 3.94 @Frequency 2.05e+9 Hz | IPC TM-650 2.5.5.13 | ||
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.00500 @Frequency 2.05e+9 Hz | 0.00500 @Frequency 2.05e+9 Hz | IPC TM-650 2.5.5.13 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 336 °C | 637 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 298 °C | 568 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 202 °C | 396 °F | B50 (50°C/h 50N); ISO 306 | ||
| Flammability, UL94 | V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | UL94 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 30.0 °C | 68.0 - 86.0 °F | |||
| 80.0 - 120 °C | 176 - 248 °F | Cavity temperature | |||
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Zone 1 | 315 - 335 °C | 599 - 635 °F | |||
| Zone 2 | 320 - 340 °C | 608 - 644 °F | |||
| Zone 3 | 325 - 355 °C | 617 - 671 °F | |||
| Zone 4 | 330 - 360 °C | 626 - 680 °F | |||
| Die Temperature | 335 - 350 °C | 635 - 662 °F | |||
| Melt Temperature | 340 °C | 644 °F | Injection molding; ISO 294 | ||
| 335 - 355 °C | 635 - 671 °F | ||||
| Mold Temperature | 100 °C | 212 °F | Injection molding; ISO 294 | ||
| Injection Velocity | 150 mm/sec | 5.91 in/sec | ISO 294 | ||
| Drying Temperature | 150 °C | 302 °F | |||
| Dry Time | 6.00 hour | 6.00 hour | |||
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual | ||
| Dew Point | <= -40.0 °C | <= -40.0 °F | Pre-drying | ||
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| Hold Pressure | 69.0 MPa | 10000 psi | ISO 294 | ||
| 50.0 - 150 MPa | 7250 - 21800 psi | ||||
| Back Pressure | 3.00 MPa | 435 psi | |||
| Screw Speed | 80.0 rpm @Diameter 40.0 mm | 80.0 rpm @Diameter 1.57 in | |||
| 140 rpm @Diameter 25.0 mm | 140 rpm @Diameter 0.984 in | ||||
| 200 rpm @Diameter 16.0 mm | 200 rpm @Diameter 0.630 in | ||||
| Hot-Working Temperature | 335 - 345 °C | 635 - 653 °F | |||
| Descriptive Properties | |||||
| Injection speed | high | ||||
| Longer pre-drying times/storage | 100° C. | <= 60 h | |||
| Short metering strokes | accumulator is recommended | to get short injection times | |||