- 密度 [g/cm3]: 1.61
- 吸水率 [%]: 0.02
- 缺口冲击强度: 1.28
- 断裂伸长率 [%]: 214
- 弯曲强度 [MPa]: 159.0
- 弯曲模量 [MPa]: 13.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.61 g/cc | 0.0582 lb/in³ | ASTM D792 |
| Water Absorption | 0.020 % | 0.020 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0015 - 0.0020 cm/cm @Thickness 3.17 mm | 0.0015 - 0.0020 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 159 MPa | 23100 psi | ASTM D638 |
| Elongation at Break | 1.0 - 3.0 % | 1.0 - 3.0 % | ASTM D638 |
| Tensile Modulus | 14.5 GPa | 2100 ksi | ASTM D638 |
| Flexural Yield Strength | 214 MPa | 31000 psi | ASTM D790 |
| Flexural Modulus | 13.1 GPa | 1900 ksi | ASTM D790 |
| Izod Impact, Notched | 1.28 J/cm @Thickness 6.35 mm | 2.40 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 243 °C | 469 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 316 - 343 °C | 601 - 649 °F | Stock |
| Mold Temperature | 135 - 149 °C | 275 - 300 °F | |
| Drying Temperature | 135 - 149 °C | 275 - 300 °F | |