- 密度 [g/cm3]: 1.5
- 吸水率 [%]: 0.02
- 缺口冲击强度: 1.6
- 断裂伸长率 [%]: 207
- 弯曲强度 [MPa]: 190.0
- 弯曲模量 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ASTM D792 |
| Water Absorption | 0.020 - 0.040 % | 0.020 - 0.040 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm @Thickness 3.17 mm | 0.0010 - 0.0020 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 190 MPa | 27600 psi | ASTM D638 |
| Elongation at Break | 1.0 - 3.0 % | 1.0 - 3.0 % | ASTM D638 |
| Tensile Modulus | 13.1 GPa | 1900 ksi | ASTM D638 |
| Flexural Yield Strength | 207 MPa | 30000 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Izod Impact, Notched | 1.60 - 2.94 J/cm @Thickness 6.35 mm | 3.00 - 5.51 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 421 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 288 - 316 °C | 550 - 601 °F | Stock |
| Mold Temperature | 93.0 - 121 °C | 199 - 250 °F | |
| Drying Temperature | 149 - 163 °C | 300 - 325 °F | |