- 密度 [g/cm3]: 1.21
- 吸水率 [%]: 0.01
- 缺口冲击强度: 1.17
- 拉伸强度 [MPa]: 105.0
- 弯曲强度 [MPa]: 105.0
- 热变形温度 [℃]: 263.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM Data |
| Water Absorption | 0.010 % | 0.010 % | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 105 MPa | 15200 psi | ASTM Data |
| Tensile Strength, Yield | 105 MPa | 15200 psi | ASTM Data |
| Tensile Modulus | 7.58 GPa | 1100 ksi | ASTM Data |
| Izod Impact, Notched | 1.17 J/cm | 2.19 ft-lb/in | ASTM Data |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 19.2 µm/m-°C @Temperature 20.0 °C | 10.7 µin/in-°F @Temperature 68.0 °F | ASTM data |
| Deflection Temperature at 0.46 MPa (66 psi) | 263 °C | 505 °F | Unannealed; ASTM Data |
| Deflection Temperature at 1.8 MPa (264 psi) | 232 °C | 450 °F | Unannealed; ASTM Data |
| Vicat Softening Point | 263 °C | 505 °F | |