- 密度 [g/cm3]: 1.25
- 成型收缩率 [%]: 0.001
- 缺口冲击强度: 12.0
- 拉伸强度 [MPa]: 120.0
- 弯曲模量 [MPa]: 9.50
- 热变形温度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 B |
| Filler Content | 30 % | 30 % | Glass |
| Moisture Absorption | 0.0100 % | 0.0100 % | 24 hours, 50% RH |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm | 0.0010 - 0.0030 in/in @Thickness 0.126 in | ISO 294 |
| 0.0020 - 0.0040 cm/cm @Thickness 1.60 mm | 0.0020 - 0.0040 in/in @Thickness 0.0630 in | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.010 cm/cm @Thickness 3.20 mm | 0.0020 - 0.010 in/in @Thickness 0.126 in | ISO 294 |
| 0.0050 - 0.0090 cm/cm @Thickness 1.60 mm | 0.0050 - 0.0090 in/in @Thickness 0.0630 in | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 120 MPa | 17400 psi | ISO 527 |
| Elongation at Break | 1.5 % | 1.5 % | ISO 527 |
| Tensile Modulus | 9.40 GPa | 1360 ksi | ISO 527 |
| Flexural Strength | 165 MPa | 23900 psi | ISO 178 |
| Flexural Modulus | 9.50 GPa | 1380 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | ISO 180 |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 3.50 J/cm² @Temperature 23.0 °C | 16.7 ft-lb/in² @Temperature 73.4 °F | ISO 179 |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature 23.0 °C | 4.76 ft-lb/in² @Temperature 73.4 °F | ISO 179 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 4.40e+12 ohm-cm | 4.40e+12 ohm-cm | IEC 93 |
| Dielectric Constant | 3.1 | 3.1 | IEC 250 |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | ASTM D149 |
| Dissipation Factor | 0.0010 | 0.0010 | IEC 250 |
| Comparative Tracking Index | 525 V | 525 V | Solution A; IEC 112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 39.0 µm/m-°C @Temperature 100 °C | 21.7 µin/in-°F @Temperature 212 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ISO 75B |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75A |
| Vicat Softening Point | 260 °C | 500 °F | A/10N; ISO 306 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 290 - 330 °C | 554 - 626 °F | pre-drying not required |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| 130 - 150 °C | 266 - 302 °F | for optimal gloss and heat resistance | |