- 密度 [g/cm3]: 1.43
- 吸水率 [%]: 0.09
- 缺口冲击强度: 9.5
- 拉伸强度 [MPa]: 115.0
- 弯曲模量 [MPa]: 11.1
- 热变形温度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 B |
| Filler Content | 30 % | 30 % | Glass |
| Water Absorption | 0.090 % | 0.090 % | 24 hours |
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 2.00 mm | 0.0020 in/in @Thickness 0.0787 in | ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm @Thickness 2.00 mm | 0.0040 in/in @Thickness 0.0787 in | ISO 294 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 115 MPa | 16700 psi | ISO 527 |
| Elongation at Break | 1.6 % | 1.6 % | ISO 527 |
| Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
| Flexural Modulus | 11.1 GPa | 1610 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 9.50 kJ/m² @Temperature 23.0 °C | 4.52 ft-lb/in² @Temperature 73.4 °F | ISO 180 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.30e+17 ohm-cm | 1.30e+17 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.2 | 3.2 | IEC 60250 |
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | ASTM D149 |
| Dissipation Factor | 0.0020 | 0.0020 | IEC 60250 |
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | ASTM D495 |
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | IEC 60112 |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | UL 746A |
| High Amp Arc Ignition, HAI | 120 arcs | 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | <= 150 mm/min | <= 5.91 in/min | UL 746A |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 29.0 µm/m-°C @Temperature 100 °C | 16.1 µin/in-°F @Temperature 212 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ISO 75B |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75A |
| Flammability, UL94 | V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | |
| 5VA @Thickness 1.75 mm | 5VA @Thickness 0.0689 in | ||
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 285 - 310 °C | 545 - 590 °F | pre-drying not required |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| 140 - 155 °C | 284 - 311 °F | for optimal gloss and heat resistance | |
| Drying Temperature | 120 °C | 248 °F | 2 to 5 hours for optimal gloss |