LATI LAESTRA G/30 30% Glass Fiber Reinforced Syndiotactic Polystyrene (SPS)

LATI LAESTRA G/30 30% Glass Fiber Reinforced Syndiotactic Polystyrene (SPS) 物性表: LATI LAESTRA G/30 30% Glass Fiber Reinforced Syndiotactic Polystyrene (SPS)物性表及特性介绍,LATI LAESTRA G/30 30% Glass Fiber Reinforced Syndiotactic Polystyrene (SPS)注塑参数详情,如需LATI LAESTRA G/30 30% Glass Fiber Reinforced Syndiotactic Polystyrene (SPS)下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.24
  • 缺口冲击强度: 0.85
  • 弯曲强度 [MPa]: 110.0
  • 弯曲模量 [MPa]: 9.10
 
Physical PropertiesMetricEnglishComments
Density 1.24 g/cc0.0448 lb/in³ISO 1183
Linear Mold Shrinkage 0.0040 cm/cm0.0040 in/inLATI
Linear Mold Shrinkage, Transverse 0.011 cm/cm0.011 in/inLATI
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength, Ultimate 110 MPa16000 psiISO 527
Flexural Modulus 9.10 GPa1320 ksiASTM D790
Izod Impact, Notched 0.850 J/cm
@Temperature 23.0 °C
1.59 ft-lb/in
@Temperature 73.4 °F
ASTM D256
 
Electrical PropertiesMetricEnglishComments
Dielectric Strength 17.0 kV/mm
@Thickness 2.00 mm
432 kV/in
@Thickness 0.0787 in
IEC 243-1
Comparative Tracking Index >= 400 V>= 400 VIEC 112
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 1.8 MPa (264 psi) 240 °C464 °FASTM D648
Flammability, UL94 HB
@Thickness 1.50 mm
HB
@Thickness 0.0591 in
 
Processing PropertiesMetricEnglishComments
Melt Temperature 300 - 325 °C572 - 617 °F
Mold Temperature 100 - 150 °C212 - 302 °F
Drying Temperature 80.0 - 100 °C176 - 212 °FNot essential. Moisture pickup may occur under adverse, high humidity conditions.
Dry Time >= 2 hour>= 2 hour
 
Descriptive Properties
Injection Speedhigh

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-32009.html

免责声明: 本文 LATI LAESTRA G/30 30% Glass Fiber Reinforced Syndiotactic Polystyrene (SPS) 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4