- 密度 [g/cm3]: 0.94
- 弯曲模量 [MPa]: 0.0850
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.940 g/cc @Temperature 23.0 °C | 0.0340 lb/in³ @Temperature 73.4 °F | ISO 1183 | ||
| Melt Index of Compound | 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 50 | 50 | ASTM D2240 | ||
| Tensile Strength at Break | 8.00 MPa | 1160 psi | ASTM D638 | ||
| Elongation at Break | 400 % | 400 % | ASTM D638 | ||
| Modulus of Elasticity | 0.104 GPa | 15.1 ksi | ASTM D638 | ||
| Flexural Modulus | 0.0850 GPa | 12.3 ksi | ASTM D638 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 106 °C | 223 °F | DSC | ||
| Vicat Softening Point | 87.0 °C @Load 0.999 kg | 189 °F @Load 2.20 lb | ASTM D1525 | ||
| Descriptive Properties | |||||
| Glycidyl Methacrylate Content (%) | 8 | IRTF (internal) | |||