- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 1.02
- 吸水率 [%]: 0.01
- 弯曲强度 [MPa]: 63.0
- 热变形温度 [℃]: 75.0
- 透光率 [%]: 91.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.010 % | 0.010 % | immersion @23°C; ISO 62 | ||
| Water Vapor Transmission | 0.0230 g/m²/day | 0.00148 g/100 in²/day | [g·mm/m2·d] @ 23°C and 85% RH; DIN 53122 | ||
| 0.250 g/m²/day | 0.0161 g/100 in²/day | Good barrier properties | |||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 245 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 473 °F | ISO 1133 | ||
| 33 g/10 min @Load 2.16 kg, Temperature 260 °C | 33 g/10 min @Load 4.76 lb, Temperature 500 °F | ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 63.0 MPa | 9140 psi | 50mm/min; ISO 527-1, 2 | ||
| Elongation at Break | 4.5 % | 4.5 % | 50mm/min; ISO 527-1, 2 | ||
| Tensile Modulus | 2.60 GPa | 377 ksi | 1mm/min; ISO 527-1, 2 | ||
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.260 J/cm² | 1.24 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 2.2 @Frequency 1.00e+10 Hz | 2.2 @Frequency 1.00e+10 Hz | |||
| Dissipation Factor | 0.00010 @Frequency 1.00e+10 Hz | 0.00010 @Frequency 1.00e+10 Hz | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ISO 75-1, 2 | ||
| Glass Transition Temp, Tg | 80.0 °C | 176 °F | |||
| Optical Properties | Metric | English | Comments | ||
| Refractive Index | 1.53 | 1.53 | |||
| Transmission, Visible | 91 % | 91 % | ISO 13468-1 | ||
| Descriptive Properties | |||||
| Pencil Hardness | HB | JIS K5401 | |||
| Resistance to Acids | Usable | ||||
| Resistance to Alcohols | Usable | ||||
| Resistance to Alkalis | Usable | ||||
| Resistance to Aromatic Solvents | Not Usable | ||||
| Resistance to Chlorinated Solvents | Not Usable | ||||
| Resistance to Esters | Usable | ||||
| Resistance to Gasoline | Not Usable | ||||
| Resistance to Ketones | Usable | ||||
| Resistance to Oils | Not Usable | ||||