- 缺口冲击强度: 0.43
- 弯曲模量 [MPa]: 5.17
- 热变形温度 [℃]: 104.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 75.8 MPa | 11000 psi | Type I, 5.1 mm/min; ASTM D638 | ||
| Elongation at Break | 1.5 % | 1.5 % | Type I, 5.1 mm/min; ASTM D638 | ||
| Tensile Modulus | 5.49 GPa | 796 ksi | 5.1 mm/min; ASTM D638 | ||
| Flexural Strength | 121 MPa | 17500 psi | 1.3 mm/min; ASTM D790 | ||
| Flexural Modulus | 5.17 GPa | 750 ksi | 1.3 mm/min; ASTM D790 | ||
| Izod Impact, Notched | 0.430 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 0.806 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | Unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C | 208 °F | Unannealed; ASTM D648 | ||
| Descriptive Properties | |||||
| Filler / Reinforcement | Glass Fiber Reinforcement | ||||
| Forms | Pellets | ||||
| Generic Material | COC | ||||
| Generic Name | Cyclic Olefin Copolymer (COC) | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||