Topas Advanced Polymers TOPAS® 6017S-04 Cyclic Olefin Copolymer (COC)

Topas Advanced Polymers TOPAS® 6017S-04 Cyclic Olefin Copolymer (COC) 物性表: Topas Advanced Polymers TOPAS® 6017S-04 Cyclic Olefin Copolymer (COC)物性表及特性介绍,Topas Advanced Polymers TOPAS® 6017S-04 Cyclic Olefin Copolymer (COC)注塑参数详情,如需Topas Advanced Polymers TOPAS® 6017S-04 Cyclic Olefin Copolymer (COC)下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 1.38
  • 密度 [g/cm3]: 1.02
  • 吸水率 [%]: 0.01
  • 拉伸强度 [MPa]: 58.0
  • 热变形温度 [℃]: 170.0
  • 透光率 [%]: 91.0
 
Physical PropertiesMetricEnglishComments
Density 1.02 g/cc0.0368 lb/in³ISO 1183
Water Absorption at Saturation 0.010 %
@Temperature 23.0 °C
0.010 %
@Temperature 73.4 °F
ISO 62
Melt Flow 1.38 g/10 min
@Load 2.16 kg,
Temperature 260 °C
1.38 g/10 min
@Load 4.76 lb,
Temperature 500 °F
ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength, Yield 58.0 MPa8410 psi5mm/min; ISO 527-2/1A
Elongation at Yield 2.4 %2.4 %5mm/min; ISO 527-2/1A
Tensile Modulus 3.00 GPa435 ksi1mm/min; ISO 527-2/1A
Charpy Impact Unnotched 1.50 J/cm²
@Temperature 23.0 °C
7.14 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.160 J/cm²
@Temperature 23.0 °C
0.761 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity >= 1.00e+16 ohm-cm>= 1.00e+16 ohm-cmIEC 60093
Dielectric Constant  2.3
@Frequency 1.00e+9 Hz
2.3
@Frequency 1.00e+9 Hz
IEC 60250
 2.35
@Frequency 1000 - 10000 Hz
2.35
@Frequency 1000 - 10000 Hz
IEC 60250
Dissipation Factor 0.0000700
@Frequency 1.00e+9 Hz
0.0000700
@Frequency 1.00e+9 Hz
IEC 60250
Comparative Tracking Index >= 600 V>= 600 VIEC 60112
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 0.46 MPa (66 psi) 170 °C338 °FISO 75-1,-2
Vicat Softening Point 178 °C352 °FB50 (50°C/h 50N); ISO 306
Glass Transition Temp, Tg 178 °C352 °F10°C/min; ISO 11357-1,-2,-3
Flammability, UL94 HB
@Thickness 1.60 mm
HB
@Thickness 0.0630 in
 
Optical PropertiesMetricEnglishComments
Refractive Index 1.531.53ISO 489
Transmission, Visible 91 %91 %ISO 13468-2
 
Processing PropertiesMetricEnglishComments
Feed Temperature <= 110 °C<= 230 °F
Nozzle Temperature 260 - 320 °C500 - 608 °F
Zone 1 250 - 280 °C482 - 536 °F
Zone 2 260 - 300 °C500 - 572 °F
Zone 3 270 - 310 °C518 - 590 °F
Zone 4 270 - 320 °C518 - 608 °F
Mold Temperature 120 - 160 °C248 - 320 °F
Injection Velocity 50.0 - 150 mm/sec1.97 - 5.91 in/secModerate to Fast
Injection Pressure 50.0 - 110 MPa7250 - 16000 psiSpecific
Hold Pressure 30.0 - 60.0 MPa4350 - 8700 psiSpecific
Back Pressure <= 15.0 MPa<= 2180 psiSpecific
Screw Speed 50 - 200 rpm50 - 200 rpm

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-32142.html

免责声明: 本文 Topas Advanced Polymers TOPAS® 6017S-04 Cyclic Olefin Copolymer (COC) 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4