- 密度 [g/cm3]: 0.49
- 吸水率 [%]: 0.1
- 缺口冲击强度: 0.246
- 断裂伸长率 [%]: 13.8
- 弯曲强度 [MPa]: 7.58
- 弯曲模量 [MPa]: 0.0138
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.490 - 1.80 g/cc | 0.0177 - 0.0649 lb/in³ | Average value: 1.14 g/cc Grade Count:26 |
| Solids Content | 100 % | 100 % | Average value: 100 % Grade Count:3 |
| Water Absorption | 0.100 - 10.0 % | 0.100 - 10.0 % | Average value: 0.911 % Grade Count:22 |
| Viscosity | 10.0 - 180000 cP | 10.0 - 180000 cP | Average value: 20300 cP Grade Count:52 |
| 46.0 - 1800 cP @Temperature 52.0 - 100 °C | 46.0 - 1800 cP @Temperature 126 - 212 °F | Average value: 717 cP Grade Count:9 | |
| Linear Mold Shrinkage | 0.00100 cm/cm | 0.00100 in/in | Average value: 0.00100 cm/cm Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 85.0 - 121 | 85.0 - 121 | Average value: 100 Grade Count:6 |
| Hardness, Shore D | 6.00 - 90.0 | 6.00 - 90.0 | Average value: 62.9 Grade Count:44 |
| >= 70.0 @Temperature 120 - 120 °C | >= 70.0 @Temperature 248 - 248 °F | Average value: 72.4 Grade Count:6 | |
| 60.0 - 85.0 @Temperature 100 - 100 °C | 60.0 - 85.0 @Temperature 212 - 212 °F | Average value: 72.4 Grade Count:7 | |
| 60.0 - 85.0 @Time 10800 - 10800 sec | 60.0 - 85.0 @Time 3.00 - 3.00 hour | Average value: 72.4 Grade Count:7 | |
| Tensile Strength, Ultimate | 7.58 - 96.5 MPa | 1100 - 14000 psi | Average value: 48.2 MPa Grade Count:56 |
| Elongation at Break | 0.700 - 400 % | 0.700 - 400 % | Average value: 25.4 % Grade Count:46 |
| Modulus of Elasticity | 0.827 - 10.0 GPa | 120 - 1450 ksi | Average value: 3.85 GPa Grade Count:16 |
| Flexural Yield Strength | 13.8 - 131 MPa | 2000 - 19000 psi | Average value: 75.1 MPa Grade Count:28 |
| Flexural Modulus | 0.0138 - 3.79 GPa | 2.00 - 550 ksi | Average value: 2.59 GPa Grade Count:10 |
| Compressive Yield Strength | 13.8 - 1930 MPa | 2000 - 280000 psi | Average value: 164 MPa Grade Count:33 |
| Shear Strength | 7.58 - 17.2 MPa | 1100 - 2500 psi | Average value: 13.2 MPa Grade Count:3 |
| Adhesive Bond Strength | 6.89 - 19.3 MPa | 1000 - 2800 psi | Average value: 13.1 MPa Grade Count:6 |
| Izod Impact, Notched | 0.246 - 1.13 J/cm | 0.460 - 2.12 ft-lb/in | Average value: 0.430 J/cm Grade Count:9 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 - 9.00e+16 ohm-cm | 1.00e+12 - 9.00e+16 ohm-cm | Average value: 6.80e+15 ohm-cm Grade Count:35 |
| 1.00e+8 - 1.00e+15 ohm-cm @Temperature 66.0 - 130 °C | 1.00e+8 - 1.00e+15 ohm-cm @Temperature 151 - 266 °F | Average value: 7.80e+13 ohm-cm Grade Count:7 | |
| Surface Resistance | 7.38e+11 - 7.85e+15 ohm | 7.38e+11 - 7.85e+15 ohm | Average value: 3.41e+15 ohm Grade Count:6 |
| Dielectric Constant | 2.79 - 4.50 | 2.79 - 4.50 | Average value: 3.52 Grade Count:30 |
| 2.66 - 5.60 @Temperature 100 - 150 °C | 2.66 - 5.60 @Temperature 212 - 302 °F | Average value: 4.06 Grade Count:12 | |
| 2.66 - 5.60 @Frequency 60.0 - 1000 Hz | 2.66 - 5.60 @Frequency 60.0 - 1000 Hz | Average value: 4.06 Grade Count:12 | |
| Dielectric Strength | 11.8 - 21.7 kV/mm | 300 - 550 kV/in | Average value: 16.3 kV/mm Grade Count:24 |
| Dissipation Factor | 0.00500 - 0.0550 | 0.00500 - 0.0550 | Average value: 0.0219 Grade Count:19 |
| 0.00700 - 0.142 @Temperature 100 - 150 °C | 0.00700 - 0.142 @Temperature 212 - 302 °F | Average value: 0.0580 Grade Count:11 | |
| 0.00700 - 0.142 @Frequency 60.0 - 60.0 Hz | 0.00700 - 0.142 @Frequency 60.0 - 60.0 Hz | Average value: 0.0580 Grade Count:11 | |
| Arc Resistance | 150 sec | 150 sec | Average value: 150 sec Grade Count:6 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 12.0 - 90.0 µm/m-°C | 6.67 - 50.0 µin/in-°F | Average value: 44.3 µm/m-°C Grade Count:14 |
| Thermal Conductivity | 0.167 - 0.795 W/m-K | 1.16 - 5.52 BTU-in/hr-ft²-°F | Average value: 0.480 W/m-K Grade Count:20 |
| Maximum Service Temperature, Air | 20.0 - 300 °C | 68.0 - 572 °F | Average value: 121 °C Grade Count:59 |
| Minimum Service Temperature, Air | -269 - -46.1 °C | -452 - -51.0 °F | Average value: -94.4 °C Grade Count:12 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | Average value: 90.0 % Grade Count:11 |
| Processing Properties | Metric | English | Comments |
| Cure Time | 1.00 - 30200 min | 0.0167 - 504 hour | Average value: 3380 min Grade Count:18 |
| 20.0 - 3600 min @Temperature 50.0 - 204 °C | 0.333 - 60.0 hour @Temperature 122 - 400 °F | Average value: 198 min Grade Count:40 | |
| Pot Life | 2.50 - 4320 min | 2.50 - 4320 min | Average value: 369 min Grade Count:66 |
| 16.0 - 420 min @Temperature 60.0 - 100 °C | 16.0 - 420 min @Temperature 140 - 212 °F | Average value: 92.4 min Grade Count:19 | |
| Shelf Life | 5.00 - 12.0 Month | 5.00 - 12.0 Month | Average value: 8.11 Month Grade Count:23 |