- 密度 [g/cm3]: 0.94
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 - 5.30 g/cc | 0.0340 - 0.191 lb/in³ | Average value: 2.75 g/cc Grade Count:96 |
| Solids Content | 68.0 - 100 % | 68.0 - 100 % | Average value: 94.5 % Grade Count:22 |
| Volatile Organic Compounds (VOC) Content | 0.000 - 591 g/l | 0.000 - 591 g/l | Average value: 88.7 g/l Grade Count:7 |
| Solubility in Water | 0.000 % | 0.000 % | Average value: 0.000 % Grade Count:4 |
| Particle Size | 2.00 - 50.0 µm | 2.00 - 50.0 µm | Average value: 30.4 µm Grade Count:43 |
| Viscosity | 220 - 2.50e+6 cP | 220 - 2.50e+6 cP | Average value: 93400 cP Grade Count:78 |
| Thickness | 25.4 - 254 microns | 1.00 - 10.0 mil | Average value: 127 microns Grade Count:7 |
| Chemical Properties | Metric | English | Comments |
| Ionic Impurities - Na (Sodium) | 0.000 - 380 ppm | 0.000 - 380 ppm | Average value: 58.4 ppm Grade Count:31 |
| Ionic Impurities - K (Potassium) | 1.00 - 50.0 ppm | 1.00 - 50.0 ppm | Average value: 17.7 ppm Grade Count:31 |
| Ionic Impurities - Cl (Chloride) | 7.00 - 295 ppm | 7.00 - 295 ppm | Average value: 109 ppm Grade Count:34 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 55.0 - 93.0 | 55.0 - 93.0 | Average value: 71.0 Grade Count:6 |
| Hardness, Shore D | 19.0 - 90.0 | 19.0 - 90.0 | Average value: 75.9 Grade Count:69 |
| Elongation at Break | 0.200 - 60.0 % | 0.200 - 60.0 % | Average value: 35.0 % Grade Count:5 |
| Modulus of Elasticity | 0.146 - 7.87 GPa | 21.2 - 1140 ksi | Average value: 3.89 GPa Grade Count:41 |
| Shear Strength | 4.48 - 35.2 MPa | 650 - 5100 psi | Average value: 14.2 MPa Grade Count:58 |
| 9.65266 - 11.0316 MPa @Temperature 65.6 - 116 °C | 1400.00 - 1600.00 psi @Temperature 150 - 240 °F | Average value: 10.1 MPa Grade Count:3 | |
| 9.65266 - 11.0316 MPa @Time 900 - 7200 sec | 1400.00 - 1600.00 psi @Time 0.250 - 2.00 hour | Average value: 10.1 MPa Grade Count:3 | |
| Adhesive Bond Strength | 0.621 - 39.3 MPa | 90.0 - 5700 psi | Average value: 8.98 MPa Grade Count:51 |
| Peel Strength | 0.877 - 3.51 kN/m | 5.00 - 20.0 pli | Average value: 2.48 kN/m Grade Count:6 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.0000800 - 100000 ohm-cm | 0.0000800 - 100000 ohm-cm | Average value: 1600 ohm-cm Grade Count:105 |
| 0.000300 - 0.00200 ohm-cm @Temperature 65.0 - 150 °C | 0.000300 - 0.00200 ohm-cm @Temperature 149 - 302 °F | Average value: 0.00364 ohm-cm Grade Count:2 | |
| <= 0.0100 ohm-cm @Temperature 65.6 - 150 °C | <= 0.0100 ohm-cm @Temperature 150 - 302 °F | Average value: 0.00364 ohm-cm Grade Count:5 | |
| <= 0.0100 ohm-cm @Time 900 - 10800 sec | <= 0.0100 ohm-cm @Time 0.250 - 3.00 hour | Average value: 0.00364 ohm-cm Grade Count:5 | |
| Surface Resistance | 0.0100 - 6.00e+6 ohm | 0.0100 - 6.00e+6 ohm | Average value: 417000 ohm Grade Count:18 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 4.50 - 280 µm/m-°C | 2.50 - 156 µin/in-°F | Average value: 78.7 µm/m-°C Grade Count:69 |
| Thermal Conductivity | 0.550 - 29.0 W/m-K | 3.82 - 201 BTU-in/hr-ft²-°F | Average value: 2.78 W/m-K Grade Count:72 |
| 10.9 - 23.0 W/m-K @Temperature 150 - 150 °C | 75.6 - 160 BTU-in/hr-ft²-°F @Temperature 302 - 302 °F | Average value: 17.0 W/m-K Grade Count:1 | |
| 10.9 - 23.0 W/m-K @Time 3600 - 3600 sec | 75.6 - 160 BTU-in/hr-ft²-°F @Time 1.00 - 1.00 hour | Average value: 17.0 W/m-K Grade Count:1 | |
| Maximum Service Temperature, Air | -150 - 538 °C | -238 - 1000 °F | Average value: 198 °C Grade Count:111 |
| Minimum Service Temperature, Air | -269 - -20.0 °C | -452 - -4.00 °F | Average value: -66.1 °C Grade Count:93 |
| Glass Transition Temp, Tg | -5.00 - 155 °C | 23.0 - 311 °F | Average value: 74.0 °C Grade Count:80 |
| Decomposition Temperature | 316 - 478 °C | 601 - 892 °F | Average value: 397 °C Grade Count:43 |
| Flash Point | 7.22 - 150 °C | 45.0 - 302 °F | Average value: 105 °C Grade Count:7 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 65.0 - 165 °C | 149 - 329 °F | Average value: 106 °C Grade Count:5 |
| Cure Time | 0.750 - 10100 min | 0.0125 - 168 hour | Average value: 1040 min Grade Count:85 |
| 0.750 - 360 min @Temperature 40.0 - 302 °C | 0.0125 - 6.00 hour @Temperature 104 - 576 °F | Average value: 61.7 min Grade Count:81 | |
| Pot Life | 10.0 - 130000 min | 10.0 - 130000 min | Average value: 5130 min Grade Count:105 |
| 2880 - 2880 min @Temperature 5.00 - 5.00 °C | 2880 - 2880 min @Temperature 41.0 - 41.0 °F | Average value: 2880 min Grade Count:1 | |
| Shelf Life | 3.00 - 12.0 Month | 3.00 - 12.0 Month | Average value: 8.93 Month Grade Count:58 |
| 6.00 - 12.0 Month @Temperature -40.0 - -40.0 °C | 6.00 - 12.0 Month @Temperature -40.0 - -40.0 °F | Average value: 11.1 Month Grade Count:14 | |
| Component Elements Properties | Metric | English | Comments |
| Carbon, C | 4.40 - 69.0 % | 4.40 - 69.0 % | Average value: 22.5 % Grade Count:10 |
| Silver, Ag | 40.0 - 85.0 % | 40.0 - 85.0 % | Average value: 66.3 % Grade Count:4 |