- 密度 [g/cm3]: 0.67
- 吸水率 [%]: 0.1
- 缺口冲击强度: 0.16
- 断裂伸长率 [%]: 180
- 弯曲强度 [MPa]: 20.7
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.670 - 2.70 g/cc | 0.0242 - 0.0975 lb/in³ | Average value: 1.74 g/cc Grade Count:82 |
| Solids Content | 100 % | 100 % | Average value: 100 % Grade Count:7 |
| Water Absorption | 0.100 - 0.150 % | 0.100 - 0.150 % | Average value: 0.125 % Grade Count:6 |
| Particle Size | 20.0 - 500 µm | 20.0 - 500 µm | Average value: 56.9 µm Grade Count:47 |
| Viscosity | 80.0 - 819000 cP | 80.0 - 819000 cP | Average value: 74500 cP Grade Count:85 |
| 1500 - 10000 cP @Temperature 40.0 - 100 °C | 1500 - 10000 cP @Temperature 104 - 212 °F | Average value: 4900 cP Grade Count:5 | |
| Storage Temperature | 4.44 - 23.9 °C | 40.0 - 75.0 °F | Average value: 19.0 °C Grade Count:4 |
| Chemical Properties | Metric | English | Comments |
| Ionic Impurities - Na (Sodium) | 9.00 - 239 ppm | 9.00 - 239 ppm | Average value: 81.1 ppm Grade Count:15 |
| Ionic Impurities - K (Potassium) | 0.000 - 50.0 ppm | 0.000 - 50.0 ppm | Average value: 24.8 ppm Grade Count:15 |
| Ionic Impurities - Cl (Chloride) | 38.0 - 267 ppm | 38.0 - 267 ppm | Average value: 148 ppm Grade Count:19 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 15.0 - 80.0 | 15.0 - 80.0 | Average value: 47.3 Grade Count:4 |
| Hardness, Shore D | 15.0 - 96.0 | 15.0 - 96.0 | Average value: 82.9 Grade Count:75 |
| >= 70.0 @Temperature 120 - 120 °C | >= 70.0 @Temperature 248 - 248 °F | Average value: 70.0 Grade Count:3 | |
| Tensile Strength, Ultimate | 20.7 - 60.0 MPa | 3000 - 8700 psi | Average value: 39.5 MPa Grade Count:8 |
| Modulus of Elasticity | 0.0179 - 17.9 GPa | 2.60 - 2600 ksi | Average value: 5.62 GPa Grade Count:53 |
| 2.362 - 4.25 GPa @Temperature 0.000 - 100 °C | 342.6 - 616 ksi @Temperature 32.0 - 212 °F | Average value: 3.31 GPa Grade Count:1 | |
| Flexural Yield Strength | 180 - 579 MPa | 26100 - 84000 psi | Average value: 404 MPa Grade Count:4 |
| Compressive Yield Strength | 68.9 - 203 MPa | 10000 - 29400 psi | Average value: 106 MPa Grade Count:4 |
| Shear Strength | 3.20 - 53.8 MPa | 464 - 7800 psi | Average value: 19.8 MPa Grade Count:49 |
| Adhesive Bond Strength | 6.21 - 27.6 MPa | 900 - 4000 psi | Average value: 14.8 MPa Grade Count:12 |
| Izod Impact, Notched | 0.160 - 53.4 J/cm | 0.300 - 100 ft-lb/in | Average value: 17.9 J/cm Grade Count:3 |
| Peel Strength | 0.789 - 1.58 kN/m | 4.50 - 9.00 pli | Average value: 1.09 kN/m Grade Count:6 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+6 - 1.00e+16 ohm-cm | 1.00e+6 - 1.00e+16 ohm-cm | Average value: 5.68e+14 ohm-cm Grade Count:64 |
| 2.00e+13 - 3.20e+13 ohm-cm @Temperature 75.0 - 75.0 °C | 2.00e+13 - 3.20e+13 ohm-cm @Temperature 167 - 167 °F | Average value: 2.90e+13 ohm-cm Grade Count:4 | |
| Surface Resistance | 1.50e+12 - 4.40e+14 ohm | 1.50e+12 - 4.40e+14 ohm | Average value: 8.57e+13 ohm Grade Count:5 |
| Dielectric Constant | 3.12 - 6.40 | 3.12 - 6.40 | Average value: 4.87 Grade Count:67 |
| Dielectric Strength | 14.8 - 78.7 kV/mm | 375 - 2000 kV/in | Average value: 23.6 kV/mm Grade Count:23 |
| Dissipation Factor | 0.00100 - 0.146 | 0.00100 - 0.146 | Average value: 0.0119 Grade Count:59 |
| Arc Resistance | 120 - 193 sec | 120 - 193 sec | Average value: 154 sec Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 14.0 - 239 µm/m-°C | 7.78 - 133 µin/in-°F | Average value: 67.8 µm/m-°C Grade Count:73 |
| CTE, linear, Transverse to Flow | 22.0 - 246 µm/m-°C | 12.2 - 137 µin/in-°F | Average value: 101 µm/m-°C Grade Count:6 |
| 175 - 192 µm/m-°C @Temperature >=160 °C | 97.2 - 107 µin/in-°F @Temperature >=320 °F | Average value: 184 µm/m-°C Grade Count:2 | |
| Thermal Conductivity | 0.100 - 5.76 W/m-K | 0.694 - 40.0 BTU-in/hr-ft²-°F | Average value: 1.13 W/m-K Grade Count:81 |
| 0.800 - 1.50 W/m-K @Temperature 80.0 - 121 °C | 5.55 - 10.4 BTU-in/hr-ft²-°F @Temperature 176 - 250 °F | Average value: 1.15 W/m-K Grade Count:2 | |
| Maximum Service Temperature, Air | 100 - 375 °C | 212 - 707 °F | Average value: 228 °C Grade Count:91 |
| Minimum Service Temperature, Air | -269 - -20.0 °C | -452 - -4.00 °F | Average value: -65.0 °C Grade Count:88 |
| Glass Transition Temp, Tg | -27.0 - 180 °C | -16.6 - 356 °F | Average value: 83.6 °C Grade Count:67 |
| Decomposition Temperature | 291 - 486 °C | 556 - 907 °F | Average value: 386 °C Grade Count:53 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:6 |
| Processing Properties | Metric | English | Comments |
| Cure Time | 4.98 - 7200 min | 0.0830 - 120 hour | Average value: 714 min Grade Count:53 |
| 1.00 - 720 min @Temperature 50.0 - 180 °C | 0.0167 - 12.0 hour @Temperature 122 - 356 °F | Average value: 83.6 min Grade Count:53 | |
| Pot Life | 5.00 - 40300 min | 5.00 - 40300 min | Average value: 8940 min Grade Count:66 |
| Shelf Life | 5.00 - 12.0 Month | 5.00 - 12.0 Month | Average value: 10.5 Month Grade Count:47 |
| 6.00 - 12.0 Month @Temperature -40.0 - 60.0 °C | 6.00 - 12.0 Month @Temperature -40.0 - 140 °F | Average value: 10.7 Month Grade Count:14 | |