- 密度 [g/cm3]: 1.9
- 吸水率 [%]: 0.2
- 缺口冲击强度: 0.35
- 弯曲模量 [MPa]: 16.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.900 g/cc | 0.0325 lb/in³ | ASTM D1895 | ||
| Density | 1.90 g/cc | 0.0686 lb/in³ | ASTM D792 | ||
| Water Absorption | 0.20 % @Temperature 50.0 °C, Time 173000 sec | 0.20 % @Temperature 122 °F, Time 48.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Barcol | 66 | 66 | ASTM D2583 | ||
| Tensile Strength at Break | 90.0 MPa | 13100 psi | ASTM D638 | ||
| Flexural Strength | 150 MPa | 21800 psi | at rupture; ASTM D790 | ||
| Flexural Modulus | 16.0 GPa | 2320 ksi | ASTM D790 | ||
| Compressive Strength | 240 MPa | 34800 psi | ASTM D695 | ||
| Izod Impact, Notched | 0.350 J/cm | 0.656 ft-lb/in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz | 3.8 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Dielectric Strength | 12.9 kV/mm @Frequency 60.0 Hz | 328 kV/in @Frequency 60.0 Hz | step-by-step, wet; ASTM D149 | ||
| 13.7 kV/mm @Frequency 60.0 Hz | 348 kV/in @Frequency 60.0 Hz | short time, wet; ASTM D149 | |||
| Dissipation Factor | 0.014 @Frequency 1.00e+6 Hz | 0.014 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Arc Resistance | 180 sec | 180 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 16.0 µm/m-°C | 8.89 µin/in-°F | ASTM E831 | ||
| CTE, linear, Transverse to Flow | 32.0 µm/m-°C | 17.8 µin/in-°F | ASTM E831 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | Post Baked; ASTM D648A | ||
| Descriptive Properties | |||||
| Colors | Black, Red, Blue | ||||
| Form | Granular | ||||
| Molding Method | Injection | ||||
| Transfer | |||||