- 密度 [g/cm3]: 2.09
- 吸水率 [%]: 0.2
- 缺口冲击强度: 0.33
- 弯曲模量 [MPa]: 23.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.900 g/cc | 0.0325 lb/in³ | ASTM D1895 | ||
| Density | 2.09 g/cc | 0.0755 lb/in³ | ASTM D792 | ||
| Water Absorption | 0.20 % @Temperature 50.0 °C, Time 173000 sec | 0.20 % @Temperature 122 °F, Time 48.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 90.0 MPa | 13100 psi | ASTM D638 | ||
| Flexural Strength | 140 MPa | 20300 psi | at rupture; ASTM D790 | ||
| Flexural Modulus | 23.0 GPa | 3340 ksi | ASTM D790 | ||
| Compressive Strength | 210 MPa | 30500 psi | ASTM D695 | ||
| Izod Impact, Notched | 0.330 J/cm | 0.618 ft-lb/in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 4.6 @Frequency 1.00e+6 Hz | 4.6 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Dielectric Strength | 13.8 kV/mm @Frequency 60.0 Hz | 351 kV/in @Frequency 60.0 Hz | step-by-step, wet; ASTM D149 | ||
| 14.5 kV/mm @Frequency 60.0 Hz | 368 kV/in @Frequency 60.0 Hz | short time, wet; ASTM D149 | |||
| Dissipation Factor | 0.035 @Frequency 1.00e+6 Hz | 0.035 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Arc Resistance | 189 sec | 189 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | As Molded; ASTM D648A | ||
| >= 282 °C | >= 540 °F | Post Baked; ASTM D648A | |||
| Descriptive Properties | |||||
| Colors | Black, Green | ||||
| Form | Granular | ||||
| Molding Method | Compression | ||||
| Transfer | |||||