- 密度 [g/cm3]: 1.5
- 断裂伸长率 [%]: 100
- 弯曲强度 [MPa]: 83.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.50 - 2.05 g/cc | 0.0542 - 0.0741 lb/in³ | Average value: 1.84 g/cc Grade Count:8 |
Spiral Flow | 38.0 - 102 cm | 15.0 - 40.2 in | Average value: 74.4 cm Grade Count:7 |
Mechanical Properties | Metric | English | Comments |
Hardness, Shore D | 74.0 - 85.0 | 74.0 - 85.0 | Average value: 78.4 Grade Count:7 |
Tensile Strength, Ultimate | 83.0 - 97.0 MPa | 12000 - 14100 psi | Average value: 90.0 MPa Grade Count:7 |
Flexural Yield Strength | 100 - 147 MPa | 14500 - 21300 psi | Average value: 128 MPa Grade Count:8 |
Electrical Properties | Metric | English | Comments |
Dielectric Constant | 3.80 - 5.20 | 3.80 - 5.20 | Average value: 4.01 Grade Count:8 |
Dielectric Strength | 16.0 - 20.0 kV/mm | 406 - 508 kV/in | Average value: 17.4 kV/mm Grade Count:7 |
Dielectric Breakdown | >= 30000 V @Temperature 90.0 - 90.0 °C | >= 30000 V @Temperature 194 - 194 °F | Average value: 30000 V Grade Count:1 |
>= 30000 V @Time 20.0 - 60.0 sec | >= 30000 V @Time 0.00556 - 0.0167 hour | Average value: 30000 V Grade Count:1 | |
Dissipation Factor | 0.00100 - 0.0400 | 0.00100 - 0.0400 | Average value: 0.00812 Grade Count:8 |
Arc Resistance | 18.0 - 190 sec | 18.0 - 190 sec | Average value: 161 sec Grade Count:7 |
Thermal Properties | Metric | English | Comments |
CTE, linear | 21.0 - 30.0 µm/m-°C | 11.7 - 16.7 µin/in-°F | Average value: 22.7 µm/m-°C Grade Count:7 |
CTE, linear, Transverse to Flow | 69.0 - 90.0 µm/m-°C | 38.3 - 50.0 µin/in-°F | Average value: 75.1 µm/m-°C Grade Count:7 |
Thermal Conductivity | 0.600 - 1.50 W/m-K | 4.16 - 10.4 BTU-in/hr-ft²-°F | Average value: 0.786 W/m-K Grade Count:7 |
Glass Transition Temp, Tg | 155 - 165 °C | 311 - 329 °F | Average value: 158 °C Grade Count:7 |
Flammability, UL94 | V-0 | V-0 | Grade Count:7 |
Processing Properties | Metric | English | Comments |
Processing Temperature | 170 - 193 °C | 338 - 379 °F | Average value: 180 °C Grade Count:7 |