- 吸水率 [%]: 1.1
- 弯曲强度 [MPa]: 67.78
- 弯曲模量 [MPa]: 3.52
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Water Absorption | 1.1 % @Time 28800 sec | 1.1 % @Time 8.00 hour | boil | ||
| Viscosity | 400 cP | 400 cP | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 85 | 85 | |||
| Tensile Strength, Ultimate | 67.78 MPa | 9831 psi | |||
| Flexural Strength | 103.05 MPa | 14946 psi | |||
| Flexural Modulus | 3.52 GPa | 510 ksi | |||
| Compressive Strength | 99.547 MPa | 14438 psi | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 60.0 - 80.0 °C | 140 - 176 °F | Deflection Temp at unknown load | ||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 - 120 min @Temperature 65.0 °C | 1.00 - 2.00 hour @Temperature 149 °F | 2nd step | ||
| 60.0 - 360 min @Temperature 80.0 - 110 °C | 1.00 - 6.00 hour @Temperature 176 - 230 °F | optional 3rd step | |||
| 1440 min @Temperature 25.0 °C | 24.0 hour @Temperature 77.0 °F | 1st step | |||
| Pot Life | 300 - 360 min | 300 - 360 min | |||
| Descriptive Properties | |||||
| Acetone Absorption (%) | 8.8 | 3 hr. boil | |||
| Color | Clear | ||||
| Parts by Weight (pbw) | 100 | AboCast | |||
| 30 | AboCure | ||||
| Ultimate Elongation (%) | 2.6 | ||||