- 密度 [g/cm3]: 1.2
- 断裂伸长率 [%]: 89.63
- 弯曲强度 [MPa]: 55.16
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | |
| Viscosity | 20000 - 40000 cP @Temperature 21.0 °C | 20000 - 40000 cP @Temperature 69.8 °F | |
| Vapor Pressure | 0.00133 bar | 1.00 torr | AboCast, at 180°C |
| <= 0.00533 bar | <= 4.00 torr | AboCure, at 60°C | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 55.16 MPa | 8000 psi | |
| Modulus of Elasticity | 2.758 GPa | 400.0 ksi | |
| Flexural Yield Strength | 89.63 MPa | 13000 psi | |
| Compressive Yield Strength | 117.2 MPa | 17000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.50e+16 ohm-cm | >= 1.50e+16 ohm-cm | |
| Dielectric Constant | 3.6 - 4.0 @Frequency 1e+6 Hz | 3.6 - 4.0 @Frequency 1e+6 Hz | |
| 3.9 - 4.3 @Frequency 50 Hz | 3.9 - 4.3 @Frequency 50 Hz | ||
| 3.9 - 4.3 @Frequency 1000 Hz | 3.9 - 4.3 @Frequency 1000 Hz | ||
| Dielectric Strength | 13.78 - 15.75 kV/mm @Thickness 3.17 mm | 350.0 - 400.0 kV/in @Thickness 0.125 in | Short time value |
| Dissipation Factor | 0.0030 - 0.0070 @Frequency 50 Hz | 0.0030 - 0.0070 @Frequency 50 Hz | |
| 0.0050 - 0.0090 @Frequency 1000 Hz | 0.0050 - 0.0090 @Frequency 1000 Hz | ||
| 0.020 - 0.040 @Frequency 1e+6 Hz | 0.020 - 0.040 @Frequency 1e+6 Hz | ||
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 160 °C | 320 °F | Deflection temperature; load unknown. |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 25.0 °C | 77.0 °F | |
| Pot Life | 60 - 180 min | 60 - 180 min | at 100°C (212°F) |
| 43200 - 86400 min | 43200 - 86400 min | at 40°C (104°F) | |
| >= 172800 min | >= 172800 min | >4 months at 20°C (68°F) | |