- 密度 [g/cm3]: 1.18
- 吸水率 [%]: 0.3
- 断裂伸长率 [%]: 96.53
- 弯曲强度 [MPa]: 65.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | |
| Water Absorption | 0.30 - 0.50 % | 0.30 - 0.50 % | (60x10X4 mm bar) after 10 days at 20°C (77°F) |
| 0.70 - 1.0 % | 0.70 - 1.0 % | (60x10X4 mm bar) after 1 hour at 100°C (212°F) | |
| Viscosity | 1600 - 2000 cP | 1600 - 2000 cP | |
| Vapor Pressure | <= 0.0000133 bar | <= 0.0100 torr | AboCure, at 20°C |
| <= 0.00133 bar | <= 1.00 torr | AboCast, at 100°C | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 65.5 MPa | 9500 psi | |
| Modulus of Elasticity | 3.447 GPa | 500.0 ksi | |
| Flexural Yield Strength | 96.53 MPa | 14000 psi | |
| Compressive Yield Strength | 103.4 MPa | 15000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.50e+16 ohm-cm | >= 1.50e+16 ohm-cm | |
| Dielectric Constant | 3.6 - 3.8 @Frequency 1e+6 Hz | 3.6 - 3.8 @Frequency 1e+6 Hz | |
| 3.8 - 4.0 @Frequency 1000 Hz | 3.8 - 4.0 @Frequency 1000 Hz | ||
| 3.9 - 4.1 @Frequency 50 Hz | 3.9 - 4.1 @Frequency 50 Hz | ||
| Dielectric Strength | 15.7 - 19.7 kV/mm @Thickness 3.17 mm | 400 - 500 kV/in @Thickness 0.125 in | Short time value |
| Dissipation Factor | 0.010 - 0.020 @Frequency 50 Hz | 0.010 - 0.020 @Frequency 50 Hz | |
| 0.010 - 0.020 @Frequency 1000 Hz | 0.010 - 0.020 @Frequency 1000 Hz | ||
| 0.020 - 0.030 @Frequency 1e+6 Hz | 0.020 - 0.030 @Frequency 1e+6 Hz | ||
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 90.0 - 95.0 µm/m-°C @Temperature 20.0 °C | 50.0 - 52.8 µin/in-°F @Temperature 68.0 °F | |
| Thermal Conductivity | 0.150 - 0.170 W/m-K | 1.04 - 1.18 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 55.0 °C | 131 °F | Deflection temperature; load unknown. |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 25.0 °C | 77.0 °F | |
| Pot Life | 150 min | 150 min | at 20°C (68°F), 30 min/40°C (105°F), 15 min/60°C (140°F) |