- 密度 [g/cm3]: 1.22
- 吸水率 [%]: 0.15
- 断裂伸长率 [%]: 131
- 弯曲强度 [MPa]: 75.84
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | |
| Water Absorption | 0.15 - 0.20 % | 0.15 - 0.20 % | (60x10X4 mm bar) after 1 hour at 100°C (212°F) |
| 0.20 - 0.30 % | 0.20 - 0.30 % | (60x10X4 mm bar) after 10 days at 20°C (77°F) | |
| Viscosity | 1000 - 2500 cP | 1000 - 2500 cP | |
| Vapor Pressure | <= 0.0000267 bar | <= 0.0200 torr | AboCure, at 50°C |
| <= 0.00133 bar | <= 1.00 torr | AboCast, at 180°C | |
| 0.00200 bar | 1.50 torr | AboCure, at 100°C | |
| 0.0293 bar | 22.0 torr | AboCure, at 165°C | |
| 0.0667 bar | 50.0 torr | albacore, at 180°C | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 75.84 MPa | 11000 psi | |
| Modulus of Elasticity | 3.102 GPa | 449.9 ksi | |
| Flexural Yield Strength | 131 MPa | 19000 psi | |
| Compressive Yield Strength | 137.9 MPa | 20000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.50e+16 ohm-cm | >= 1.50e+16 ohm-cm | |
| Dielectric Constant | 3.3 - 3.5 @Frequency 1e+6 Hz | 3.3 - 3.5 @Frequency 1e+6 Hz | |
| 3.4 - 3.6 @Frequency 1000 Hz | 3.4 - 3.6 @Frequency 1000 Hz | ||
| 3.6 - 3.8 @Frequency 50 Hz | 3.6 - 3.8 @Frequency 50 Hz | ||
| Dielectric Strength | 13.8 - 17.7 kV/mm @Thickness 3.17 mm | 350 - 450 kV/in @Thickness 0.125 in | Short time value |
| Dissipation Factor | 0.0020 - 0.0040 @Frequency 50 Hz | 0.0020 - 0.0040 @Frequency 50 Hz | |
| 0.0030 - 0.0050 @Frequency 1000 Hz | 0.0030 - 0.0050 @Frequency 1000 Hz | ||
| 0.010 - 0.015 @Frequency 1e+6 Hz | 0.010 - 0.015 @Frequency 1e+6 Hz | ||
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 55.0 - 65.0 µm/m-°C @Temperature 20.0 °C | 30.6 - 36.1 µin/in-°F @Temperature 68.0 °F | |
| Maximum Service Temperature, Air | 150 °C | 302 °F | Deflection temperature; load unknown. |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 25.0 °C | 77.0 °F | |
| Pot Life | 420 - 600 min | 420 - 600 min | at 120°C (248°F) |
| 21600 - 28800 min | 21600 - 28800 min | at 20°C (68°F) | |