- 密度 [g/cm3]: 0.962
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.962 g/cc | 0.0348 lb/in³ | |||
| Solids Content | 47.4 % | 47.4 % | Total | ||
| Viscosity Measurement | 25 | 25 | secs., #4 Ford cup. | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | >= 60 % | >= 60 % | Direction not specified | ||
| Impact Test | 18.1 J | 13.3 ft-lb | Forward/reverse | ||
| Optical Properties | Metric | English | Comments | ||
| Gloss | 60 % | 60 % | 3 mils, 48 hours | ||
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified | ||
| Processing Properties | Metric | English | Comments | ||
| Dry Time | 3 hour | 3 hour | Tackfree, at room temperature, minutes w/heat | ||
| Pot Life | 60 - 75 min | 60 - 75 min | |||
| Shelf Life | >= 12.0 Month | >= 12.0 Month | |||
| Descriptive Properties | |||||
| Adhesion | Excellent | Crosshatch | |||
| Induction Period | 40-60 minutes | ||||
| Mandrel Flexibility | Passes 1/8" | ||||
| Pencil Hardness | 3 | Overnight at room temperature | |||
| 4H | 7 days | ||||