- 吸水率 [%]: 0.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Absorption | 0.10 - 0.50 % | 0.10 - 0.50 % | 24-200 hours |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | >= 90 | >= 90 | |
| Tensile Strength at Break | 49.6 MPa | 7200 psi | |
| Elongation at Break | 1.8 % | 1.8 % | |
| Flexural Strength | 60.7 MPa | 8800 psi | |
| Compressive Strength | 108 MPa | 15700 psi | |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.586 - 0.669 W/m-K | 4.06 - 4.64 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 70.0 °C | 158 °F | Deflection temperature after room temperature cure |
| 115 °C | 239 °F | Deflection temperature after post-cure | |
| Processing Properties | Metric | English | Comments |
| Pot Life | 30 - 45 min | 30 - 45 min | 1-2 lbs at 25°C |