- 密度 [g/cm3]: 1.19
- 吸水率 [%]: 0.3
- 断裂伸长率 [%]: 124.1
- 弯曲强度 [MPa]: 65.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | |
| Water Absorption | 0.30 - 0.40 % | 0.30 - 0.40 % | (60x10X4 mm bar) after 10 days at 20°C (77°F) |
| 0.60 - 1.0 % | 0.60 - 1.0 % | (60x10X4 mm bar) after 1 hour at 100°C (212°F) | |
| Viscosity | 4500 - 6000 cP | 4500 - 6000 cP | |
| Vapor Pressure | <= 0.0000133 bar | <= 0.0100 torr | AboCure, at 20°C |
| 0.00133 bar | 1.00 torr | AboCast, at 180°C | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 65.5 MPa | 9500 psi | |
| Modulus of Elasticity | 3.447 GPa | 500.0 ksi | |
| Flexural Yield Strength | 124.1 MPa | 18000 psi | |
| Compressive Yield Strength | 124.1 MPa | 18000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.50e+16 ohm-cm | >= 1.50e+16 ohm-cm | |
| Dielectric Constant | 3.65 - 3.85 @Frequency 1e+6 Hz | 3.65 - 3.85 @Frequency 1e+6 Hz | |
| 3.8 - 4.0 @Frequency 1000 Hz | 3.8 - 4.0 @Frequency 1000 Hz | ||
| 3.85 - 4.05 @Frequency 50 Hz | 3.85 - 4.05 @Frequency 50 Hz | ||
| Dielectric Strength | 15.7 - 19.7 kV/mm @Thickness 3.17 mm | 400 - 500 kV/in @Thickness 0.125 in | Short time value |
| Dissipation Factor | 0.0050 - 0.010 @Frequency 50 Hz | 0.0050 - 0.010 @Frequency 50 Hz | |
| 0.010 - 0.015 @Frequency 1000 Hz | 0.010 - 0.015 @Frequency 1000 Hz | ||
| 0.025 - 0.030 @Frequency 1e+6 Hz | 0.025 - 0.030 @Frequency 1e+6 Hz | ||
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 65.0 - 70.0 µm/m-°C @Temperature 20.0 °C | 36.1 - 38.9 µin/in-°F @Temperature 68.0 °F | |
| Thermal Conductivity | 0.190 - 21.0 W/m-K | 1.32 - 146 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Deflection temperature; load unknown. |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 25.0 °C | 77.0 °F | |
| Pot Life | 10 min | 10 min | at 60°C (140°F) |
| 20 min | 20 min | at 40°C (104°F) | |
| 45 min | 45 min | at 20°C (68°F) | |