ACC EP AEP EPI Engineered Polymers

ACC EP AEP EPI Engineered Polymers 物性表: ACC EP AEP EPI Engineered Polymers物性表及特性介绍,ACC EP AEP EPI Engineered Polymers注塑参数详情,如需ACC EP AEP EPI Engineered Polymers下载, 可到相关下载区下载
  • 拉伸强度 [MPa]: 24.8
 
Physical PropertiesMetricEnglishComments
Viscosity  1100 cP
@Temperature 75.0 °C
1100 cP
@Temperature 167 °F
A Side
 1575 cP
@Temperature 75.0 °C
1575 cP
@Temperature 167 °F
B Side
 
Mechanical PropertiesMetricEnglishComments
Hardness, Shore D 4545ASTM 2240
Tensile Strength, Yield 24.8 MPa3590 psiASTM D412
Elongation at Break 200 %200 %ASTM D412
Adhesive Bond Strength >= 1.72 MPa>= 250 psiWood (no primer), Delamination; ASTM D4541 Elcometer
 >= 2.07 MPa>= 300 psiConcrete (no primer) Concrete Failure; ASTM D4541 Elcometer
 >= 2.07 MPa>= 300 psiConcrete (primer), Concrete Failure; ASTM D4541 Elcometer
 >= 2.07 MPa>= 300 psiConcrete (epoxy), Concrete Failure; ASTM D4541 Elcometer
 >= 6.21 MPa>= 900 psiSteel (no primer), Substrate Failure; ASTM D4541 Elcometer
 >= 10.3 MPa>= 1500 psiSteel (epoxy primer), Primer Failure; ASTM D4541 Elcometer
Tear Strength 78.9 kN/m450 pliASTM D412
Taber Abrasion, mg/1000 Cycles 4545CS17 WHEEL, 1kg per 1000 cycles; ASTM D4060
 
Thermal PropertiesMetricEnglishComments
Flash Point >= 93.3 °C>= 200 °FASTM Pensky-Martin
 
Processing PropertiesMetricEnglishComments
Cure Time >= 45.0 min>= 0.750 hourTack Free Time
Pot Life 15 min15 min
 
Descriptive Properties
ColorAll primary colors.
Flexibility PassASTM D1737, 1/8"Mandrel
Resistance to 1,1,1-TrichlorethaneConditional
Resistance to Acetic Acid (100%)Conditional
Resistance to AcetoneConditional
Resistance to Ammonium Hydroxide (50%)Recommended Conditional
Resistance to Benzene Conditional
Resistance to Brine-Saturated H2ORecommended Resistance to Brine-Saturated H2O (310g/l)
Resistance to Chlorinated H2ORecommended
Resistance to Clorox® (10%) H2ORecommended
Resistance to Diesel Fuel Recommended Conditional
Resistance to GasolineRecommended Conditional
Resistance to Gasoline/ 5% MethanolRecommended Conditional
Resistance to Gasoline/5% MTBERecommended Conditional
Resistance to H2ORecommended
Resistance to H2O (14 days at 82°C)Recommended Conditional
Resistance to Hydraulic Fluid (oil) Recommended Conditional
Resistance to Hydrochloric Acid (20%)Recommended
Resistance to Hydrofluoric Acid(10%)Not Recommended
Resistance to Isopropyl AlcoholRecommended
Resistance to Lactic AcidRecommended Conditional
Resistance to MEKRecommended Conditional
Resistance to MethanolRecommended
Resistance to Methylene Chloride Conditional
Resistance to Mineral Spirits Recommended Conditional
Resistance to Motor OilRecommended
Resistance to MTEBConditional
Resistance to Muriatic Acid (10%)Recommended
Resistance to NaCl/H2O (10%)Recommended
Resistance to Nitric Acid (20%)Not Recommended
Resistance to Phosphoric Acid (10%)Recommended
Resistance to Phosphoric Acid (50%)Not Recommended
Resistance to Potassium Hydroxide (10%)Recommended
Resistance to Potassium Hydroxide (20%)Recommended, Discoloration
Resistance to Propylene CarbonateRecommended Conditional
Resistance to Skydrol® Conditional
Resistance to Sodium BicarbonateRecommended
Resistance to Sodium Hydroxide (25%)Recommended
Resistance to Sodium Hydroxide (50%)Recommended, Discoloration
Resistance to Sodium Hypochlorite (10%)Recommended
Resistance to Stearic AcidRecommended
Resistance to Sugar/H2ORecommended
Resistance to Sulfuric Acid (>50%)Recommended Conditional
Resistance to Sulfuric Acid (10%)Recommended
Resistance to TolueneRecommended
Resistance to Trisodium PhosphateRecommended
Resistance to Vinegar/ H2O (5%)Recommended
Resistance to Xylene Recommended Conditional

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-32409.html

免责声明: 本文 ACC EP AEP EPI Engineered Polymers 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4