- 弯曲强度 [MPa]: 38.6
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 10400 cP | 10400 cP | Mixed | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 84 | 84 | |||
| Tensile Strength, Ultimate | 38.6 MPa | 5600 psi | after optimum cure | ||
| Elongation at Break | 12.5 % | 12.5 % | |||
| Adhesive Bond Strength | 36.2 MPa | 5250 psi | Steel-Steel; after optimum cure | ||
| 5.17 MPa @Temperature 82.2 °C | 750 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| 12.4 MPa @Temperature 25.0 °C | 1800 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| 16.9 MPa @Temperature -54.4 °C | 2450 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 18.0 µm/m-°C @Temperature 20.0 °C | 10.0 µin/in-°F @Temperature 68.0 °F | |||
| Glass Transition Temp, Tg | 65.0 °C | 149 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 22.2 °C | 72.0 °F | Room Temp Cure Possible | ||
| 73.9 °C | 165 °F | Optimum cure is 2 hr. @ 165°F | |||
| 149 °C | 300 °F | Fast cure is 5 min. @ 300°F | |||
| Pot Life | 90 min | 90 min | Max working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | Amber | ||||
| Mix Ratio | 1/1 | By Weight | |||