- 弯曲强度 [MPa]: 30.3
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 20000 cP | 20000 cP | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 82 | 82 | |||
| Tensile Strength, Ultimate | 30.3 MPa | 4400 psi | after optimum cure | ||
| Elongation at Break | 1.2 % | 1.2 % | |||
| Adhesive Bond Strength | 34.8 MPa | 5050 psi | Steel-Steel; after optimum cure | ||
| 6.21 MPa @Temperature 82.2 °C | 900 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| 6.89 MPa @Temperature -54.4 °C | 1000 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| 14.8 MPa @Temperature 25.0 °C | 2150 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 58.0 µm/m-°C @Temperature 20.0 °C | 32.2 µin/in-°F @Temperature 68.0 °F | |||
| Glass Transition Temp, Tg | 144 °C | 291 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 204 °C | 400 °F | Optimum cure is 1 hr. @ 400°F | ||
| Pot Life | 99999 min | 99999 min | Indefinite working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | Amber | ||||
| Mix Ratio | 1 Part | ||||