- 密度 [g/cm3]: 1.35
- 吸水率 [%]: 0.15
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 Method A | ||
| Water Absorption | 0.15 % | 0.15 % | IPC TM-650 2.6.2.1 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 44.8 MPa | 6500 psi | IPC TM-650 2.4.18.3 | ||
| Modulus of Elasticity | 17.9 GPa | 2600 ksi | IPC TM-650 2.4.18.3 | ||
| Flexural Strength | 579 MPa | 84000 psi | IPC TM-650 2.4.4 | ||
| Peel Strength | 1.12 kN/m | 6.40 pli | To Copper (1 oz./35 micron); After Process Solutions; IPC TM-650 2.4.8 | ||
| 1.17 kN/m | 6.70 pli | To Copper (1 oz./35 micron); After Thermal Stress; IPC TM-650 2.4.8 | |||
| 1.17 kN/m | 6.70 pli | To Copper (1 oz./35 micron); At Elevated Temperatures; IPC TM-650 2.4.8.2 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 2.60e+13 ohm-cm | 2.60e+13 ohm-cm | C96/35/90; IPC TM-650 2.5.17.1 | ||
| 3.30e+13 ohm-cm | 3.30e+13 ohm-cm | E24/125; IPC TM-650 2.5.17.1 | |||
| Surface Resistance | 4.00e+12 ohm | 4.00e+12 ohm | E24/125; IPC TM-650 2.5.17.1 | ||
| 2.90e+13 ohm | 2.90e+13 ohm | C96/35/90; IPC TM-650 2.5.17.1 | |||
| Dielectric Constant | 4.1 @Frequency 1.00e+9 Hz | 4.1 @Frequency 1.00e+9 Hz | may vary with resin %; IPC TM-650 2.5.5.9 | ||
| 4.2 @Frequency 1.00e+6 Hz | 4.2 @Frequency 1.00e+6 Hz | may vary with resin %; IPC TM-650 2.5.5.3 | |||
| Dielectric Strength | 39.4 kV/mm | 1000 kV/in | IPC TM-650 2.5.6.2 | ||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IPC TM-650 2.5.5.3 | ||
| 0.020 @Frequency 1.00e+9 Hz | 0.020 @Frequency 1.00e+9 Hz | IPC TM-650 2.5.5.9 | |||
| Arc Resistance | >= 120 sec | >= 120 sec | IPC TM-650 2.5.1 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 14.0 µm/m-°C | 7.78 µin/in-°F | IPC TM-650 2.4.41 | ||
| CTE, linear, Transverse to Flow | 44.0 µm/m-°C | 24.4 µin/in-°F | z, below Tg; IPC TM-650 2.4.24 | ||
| 245 µm/m-°C | 136 µin/in-°F | z, above Tg; IPC TM-650 2.4.24 | |||
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | ASTM E1461 | ||
| Glass Transition Temp, Tg | 166 °C | 331 °F | TMA; IPC TM-650 2.4.24 | ||
| 170 °C | 338 °F | DSC; IPC TM-650 2.4.25 | |||
| Decomposition Temperature | 354 °C | 669 °F | Onset; IPC TM-650 2.4.24.6 | ||
| 368 °C | 694 °F | 5 percent; IPC TM-650 2.4.24.6 | |||
| Flammability, UL94 | V-0 | V-0 | |||
| Descriptive Properties | |||||
| IPC Delamination - T260 (minutes) | > 60 | IPC TM-650 2.4.24.1 | |||
| IPC Delamination - T288 (minutes) | > 30 | IPC TM-650 2.4.24.1 | |||
| IPC Delamination - T300 (minutes) | 15 | IPC TM-650 2.4.24.1 | |||
| Z-Axis Expansion (%) | 2.6 | IPC TM-650 2.4.24 (50-260°C) | |||