- 密度 [g/cm3]: 2.05
- 弯曲强度 [MPa]: 97.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.05 g/cc | 0.0741 lb/in³ | |
| Spiral Flow | 64.0 - 88.0 cm | 25.2 - 34.6 in | 177°C/1000 psi |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 85 | 85 | |
| Tensile Strength, Ultimate | 97.0 MPa | 14100 psi | |
| Flexural Strength | 138 MPa | 20000 psi | |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.9 @Frequency 1000 Hz | 3.9 @Frequency 1000 Hz | |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | |
| Dissipation Factor | 0.0060 @Frequency 1000 Hz | 0.0060 @Frequency 1000 Hz | |
| Arc Resistance | 190 sec | 190 sec | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.0 µm/m-°C @Temperature 20.0 °C | 16.7 µin/in-°F @Temperature 68.0 °F | |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 20.0 °C | 44.4 µin/in-°F @Temperature 68.0 °F | |
| Thermal Conductivity | 1.50 W/m-K | 10.4 BTU-in/hr-ft²-°F | |
| Glass Transition Temp, Tg | 165 °C | 329 °F | |
| Flammability, UL94 | V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | |
| V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | ||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 170 - 185 °C | 338 - 365 °F | Molding temperature |