Cookson Group Plaskon® 3300SH Mineral Filled Epoxy Molding Compound

Cookson Group Plaskon® 3300SH Mineral Filled Epoxy Molding Compound 物性表: Cookson Group Plaskon® 3300SH Mineral Filled Epoxy Molding Compound物性表及特性介绍,Cookson Group Plaskon® 3300SH Mineral Filled Epoxy Molding Compound注塑参数详情,如需Cookson Group Plaskon® 3300SH Mineral Filled Epoxy Molding Compound下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.86
  • 弯曲强度 [MPa]: 83.0
  • 弯曲模量 [MPa]: 16.0
 
Physical PropertiesMetricEnglishComments
Density 1.86 g/cc0.0672 lb/in³
Spiral Flow 78.0 - 102 cm30.7 - 40.2 in177°C/1000 psi
 
Mechanical PropertiesMetricEnglishComments
Hardness, Shore D 7575
Tensile Strength, Ultimate 83.0 MPa12000 psi
Flexural Strength 124 MPa18000 psi
Flexural Modulus 16.0 GPa2320 ksi
 
Electrical PropertiesMetricEnglishComments
Dielectric Constant 3.8
@Frequency 1000 Hz
3.8
@Frequency 1000 Hz
Dielectric Strength 16.0 kV/mm406 kV/in
Dissipation Factor 0.0020
@Frequency 1000 Hz
0.0020
@Frequency 1000 Hz
Arc Resistance 18 sec18 sec
 
Thermal PropertiesMetricEnglishComments
CTE, linear 21.0 µm/m-°C
@Temperature 20.0 °C
11.7 µin/in-°F
@Temperature 68.0 °F
CTE, linear, Transverse to Flow 69.0 µm/m-°C
@Temperature 20.0 °C
38.3 µin/in-°F
@Temperature 68.0 °F
Thermal Conductivity 0.700 W/m-K4.86 BTU-in/hr-ft²-°F
Glass Transition Temp, Tg 155 °C311 °F
Flammability, UL94  V-0
@Thickness 3.20 mm
V-0
@Thickness 0.126 in
 V-0
@Thickness 3.20 mm
V-0
@Thickness 0.126 in
 
Processing PropertiesMetricEnglishComments
Processing Temperature 170 - 190 °C338 - 374 °FMolding temperature

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-32779.html

免责声明: 本文 Cookson Group Plaskon® 3300SH Mineral Filled Epoxy Molding Compound 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4