- 弯曲强度 [MPa]: 145.0
- 弯曲模量 [MPa]: 13.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.85 g/cc | 1.85 g/cc | |
| Filler Content | 64 % | 64 % | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 70 | 70 | |
| Tensile Strength, Ultimate | 145 MPa | 21000 psi | 45° stress angle |
| 483 MPa | 70000 psi | 90° stress angle | |
| 483 MPa | 70000 psi | 0° stress angle | |
| Tensile Modulus | 10.3 GPa | 1500 ksi | 45° stress angle |
| 23.4 GPa | 3400 ksi | 0° stress angle | |
| 24.1 GPa | 3500 ksi | 90° stress angle | |
| Flexural Strength | 310 MPa | 45000 psi | 45° stress angle |
| 758 MPa | 110000 psi | 90° stress angle | |
| 758 MPa | 110000 psi | 0° stress angle | |
| Flexural Modulus | 13.8 GPa | 2000 ksi | 45° stress angle |
| 24.1 GPa | 3500 ksi | 90° stress angle | |
| 24.1 GPa | 3500 ksi | 0° stress angle | |
| Compressive Strength | 207 MPa | 30000 psi | 45° stress angle |
| 689 MPa | 100000 psi | 90° stress angle | |
| 689 MPa | 100000 psi | 0° stress angle | |
| Fatigue Strength | 159 MPa @# of Cycles 1.00e+8 | 23000 psi @# of Cycles 1.00e+8 | Flexural Fatigue (SN) |
| 172 MPa @# of Cycles 1.00e+7 | 25000 psi @# of Cycles 1.00e+7 | Flexural Fatigue (SN) | |
| 214 MPa @# of Cycles 1.00e+6 | 31000 psi @# of Cycles 1.00e+6 | Flexural Fatigue (SN) | |
| 262 MPa @# of Cycles 100000 | 38000 psi @# of Cycles 100000 | Flexural Fatigue (SN) | |
| 310 MPa @# of Cycles 10000 | 45000 psi @# of Cycles 10000 | Flexural Fatigue (SN) | |
| 407 MPa @# of Cycles 1000 | 59000 psi @# of Cycles 1000 | Flexural Fatigue (SN) | |
| Shear Modulus | 62.1 GPa | 9000 ksi | Short Beam; 0° stress angle; span/depth 5:1; ASTM D2344-76; span/depth 5:1 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 4.90e+17 ohm-cm | 4.90e+17 ohm-cm | 50% RH and at 90% RH |
| Insulation Resistance | 5.30e+15 ohm | 5.30e+15 ohm | 50% RH |
| 6.80e+10 ohm @Temperature 150 °C | 6.80e+10 ohm @Temperature 302 °F | 50% RH | |
| 6.20e+11 ohm @Temperature 120 °C | 6.20e+11 ohm @Temperature 248 °F | 50% RH | |
| 9.70e+12 ohm @Temperature 60.0 °C | 9.70e+12 ohm @Temperature 140 °F | 90% RH | |
| 2.70e+14 ohm @Temperature 60.0 °C | 2.70e+14 ohm @Temperature 140 °F | 50% RH | |
| 3.30e+14 ohm @Temperature 23.0 °C | 3.30e+14 ohm @Temperature 73.4 °F | 90% RH | |
| Dielectric Constant | 4.8 @Frequency 1e+6 Hz | 4.8 @Frequency 1e+6 Hz | 50% RH |
| 5.2 @Frequency 1000 Hz | 5.2 @Frequency 1000 Hz | 50% RH | |
| 4.4 @Frequency 3.00e+7 Hz, Temperature 23.0 °C | 4.4 @Frequency 3.00e+7 Hz, Temperature 73.4 °F | 50% RH | |
| 5.1 @Frequency 100000 Hz, Temperature 23.0 °C | 5.1 @Frequency 100000 Hz, Temperature 73.4 °F | 50% RH | |
| 5.3 @Frequency 60.0 Hz, Temperature 23.0 °C | 5.3 @Frequency 60.0 Hz, Temperature 73.4 °F | 50% RH | |
| 5.5 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 5.5 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 90% RH | |
| 5.7 @Frequency 1000 Hz, Temperature 60.0 °C | 5.7 @Frequency 1000 Hz, Temperature 140 °F | 50% RH | |
| 6.1 @Frequency 1000 Hz, Temperature 120 °C | 6.1 @Frequency 1000 Hz, Temperature 248 °F | 50% RH | |
| 6.5 @Frequency 1000 Hz, Temperature 23.0 °C | 6.5 @Frequency 1000 Hz, Temperature 73.4 °F | 90% RH | |
| 6.8 @Frequency 1000 Hz, Temperature 60.0 °C | 6.8 @Frequency 1000 Hz, Temperature 140 °F | 90% RH | |
| 7.0 @Frequency 60.0 Hz, Temperature 23.0 °C | 7.0 @Frequency 60.0 Hz, Temperature 73.4 °F | 90% RH | |
| 7.3 @Frequency 1000 Hz, Temperature 150 °C | 7.3 @Frequency 1000 Hz, Temperature 302 °F | 50% RH | |
| Dielectric Strength | 24.4 kV/mm | 620 kV/in | 50% RH |
| Dissipation Factor | 0.0060 @Frequency 1000 Hz | 0.0060 @Frequency 1000 Hz | 50% RH |
| 0.017 @Frequency 1e+6 Hz | 0.017 @Frequency 1e+6 Hz | 50% RH | |
| 0.0033 @Frequency 1000 Hz, Temperature 120 °C | 0.0033 @Frequency 1000 Hz, Temperature 248 °F | 50% RH | |
| 0.0052 @Frequency 60.0 Hz, Temperature 23.0 °C | 0.0052 @Frequency 60.0 Hz, Temperature 73.4 °F | 50% RH | |
| 0.0087 @Frequency 1000 Hz, Temperature 60.0 °C | 0.0087 @Frequency 1000 Hz, Temperature 140 °F | 50% RH | |
| 0.014 @Frequency 100000 Hz, Temperature 23.0 °C | 0.014 @Frequency 100000 Hz, Temperature 73.4 °F | 50% RH | |
| 0.019 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.019 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 90% RH | |
| 0.023 @Frequency 3.00e+7 Hz, Temperature 23.0 °C | 0.023 @Frequency 3.00e+7 Hz, Temperature 73.4 °F | 50% RH | |
| 0.036 @Frequency 60.0 Hz, Temperature 23.0 °C | 0.036 @Frequency 60.0 Hz, Temperature 73.4 °F | 90% RH | |
| 0.050 @Frequency 1000 Hz, Temperature 23.0 °C | 0.050 @Frequency 1000 Hz, Temperature 73.4 °F | 90% RH | |
| 0.054 @Frequency 1000 Hz, Temperature 60.0 °C | 0.054 @Frequency 1000 Hz, Temperature 140 °F | 90% RH | |
| 0.13 @Frequency 1000 Hz, Temperature 150 °C | 0.13 @Frequency 1000 Hz, Temperature 302 °F | 50% RH | |
| Arc Resistance | 20 sec | 20 sec | with filaments; 50% RH and at 90% RH |
| 80 sec | 80 sec | across filaments; 50% RH and at 90% RH | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 12.8 µm/m-°C @Temperature -34.4 - 93.3 °C | 7.10 µin/in-°F @Temperature -30.0 - 200 °F | parallel to lengthwise filaments; ASTM D696-42T |
| 12.8 µm/m-°C @Temperature -34.4 - 93.3 °C | 7.10 µin/in-°F @Temperature -30.0 - 200 °F | parallel to crosswise filaments; ASTM D696-42T | |
| Specific Heat Capacity | 0.879 J/g-°C | 0.210 BTU/lb-°F | |
| Thermal Conductivity | 0.334 W/m-K @Temperature 7.22 °C | 2.32 BTU-in/hr-ft²-°F @Temperature 45.0 °F | on 1 inch thick isotropic laminate |
| 0.336 W/m-K @Temperature 2.22 °C | 2.33 BTU-in/hr-ft²-°F @Temperature 36.0 °F | on 1 inch thick isotropic laminate | |
| 0.342 W/m-K @Temperature 51.7 °C | 2.37 BTU-in/hr-ft²-°F @Temperature 125 °F | on 1 inch thick isotropic laminate | |
| 0.346 W/m-K @Temperature 85.6 °C | 2.40 BTU-in/hr-ft²-°F @Temperature 186 °F | on 1 inch thick isotropic laminate | |