- 密度 [g/cm3]: 1.4
- 断裂伸长率 [%]: 165
- 弯曲强度 [MPa]: 103.0
- 弯曲模量 [MPa]: 13.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | Cloth 1.42 g/cc per He measurement |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 60 | 60 | |
| Tensile Strength, Ultimate | 103 MPa | 14900 psi | |
| Tensile Modulus | 13.0 GPa | 1890 ksi | |
| Flexural Yield Strength | 165 MPa | 23900 psi | |
| Flexural Modulus | 13.0 GPa | 1890 ksi | |
| Compressive Yield Strength | 110 MPa | 16000 psi | |
| Compressive Modulus | 15.0 GPa | 2180 ksi | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 11.0 µm/m-°C @Temperature 20.0 °C | 6.11 µin/in-°F @Temperature 68.0 °F | Warp |
| Specific Heat Capacity | 1.00 J/g-°C | 0.239 BTU/lb-°F | |
| Thermal Conductivity | 10.0 W/m-K | 69.4 BTU-in/hr-ft²-°F | |