- 密度 [g/cm3]: 1.29
- 弯曲强度 [MPa]: 30.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 - 1.35 g/cc | 0.0466 - 0.0488 lb/in³ | |
| Solids Content | >= 99 % | >= 99 % | |
| Viscosity | 900000 cP @Shear Rate 1.00 1/s, Temperature 40.0 °C | 900000 cP @Shear Rate 1.00 1/s, Temperature 104 °F | cone/plate |
| 2.50e+6 cP @Shear Rate 1.00 1/s, Temperature 23.0 °C | 2.50e+6 cP @Shear Rate 1.00 1/s, Temperature 73.4 °F | cone/plate | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | ISO 527-1 |
| Elongation at Break | 3.5 % | 3.5 % | ISO 527-1 |
| Modulus of Elasticity | 2.50 GPa | 363 ksi | ISO 527-1 |
| Adhesive Bond Strength | 13.6 MPa @Thickness 0.750 mm | 1970 psi @Thickness 0.0295 in | Lap Shear (25 x 10 x 0.2 mm) (CRS St 1203); EN 1465 |
| 20.9 MPa @Thickness 1.50 mm | 3030 psi @Thickness 0.0591 in | Lap Shear (25 x 10 x 0.2 mm) (CRS St 1203); EN 1465 | |
| Peel Strength | 3.40 kN/m | 19.4 pli | T-Peel (CRS St 1203, 0.5mm) |
| 7.00 kN/m | 39.9 pli | Impact Peel | |
| Thermal Properties | Metric | English | Comments |
| Flash Point | >= 150 °C | >= 302 °F | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 30.0 min | 0.500 hour | 180°C |