- 密度 [g/cm3]: 1.75
- 吸水率 [%]: 0.02
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.75 g/cc @Thickness >=0.000 mm | 0.0632 lb/in³ @Thickness >=0.000 in | 24hr/23°C/50% RH; ISO 1183-A; IEC/EN 61212-2 7.3 |
| Water Absorption | 0.020 % | 0.020 % | 24hr/50°C+24hr in water at 23°C; ISO 62-1; IEC/EN 61212-2 7.2 |
| Mechanical Properties | Metric | English | Comments |
| Flexural Strength | 350 MPa @Diameter >=100 mm | 50800 psi @Diameter >=3.94 in | 24hr/23°C/50% RH, 230 Mpa measured at 150°C; ISO 178; IEC/EN 61212-2 5.1 |
| Compressive Strength | 200 MPa @Temperature 23.0 °C, Time 86400 sec | 29000 psi @Temperature 73.4 °F, Time 24.0 hour | 50% RH, Axial; ISO 604; IEC/EN 61212-2 5.2 |
| Adhesive Bond Strength | 400 MPa @Diameter <=100 mm | 58000 psi @Diameter <=3.94 in | 24hr/23°C/50% RH; IEC 60212-2; IEC/EN 61212-2 5.3 |
| Electrical Properties | Metric | English | Comments |
| Insulation Resistance | 1.00e+10 ohm @Diameter 8.00 - 10.0 mm | 1.00e+10 ohm @Diameter 0.315 - 0.394 in | 24hr/50°C+24h in water at 23°C; IEC; IEC/EN 61212-2 6.2 |
| Dielectric Constant | 4.5 @Frequency 50.0 Hz | 4.5 @Frequency 50.0 Hz | 96hr/105°C+1hr/23°C/20%RH; IEC 250; IEC/EN 61212-2 6.3 |
| 4.5 @Frequency 1.00e+6 Hz | 4.5 @Frequency 1.00e+6 Hz | 96hr/105°C+1hr/23°C/20%RH; IEC 250; IEC/EN 61212-2 6.3 | |
| Dielectric Strength | 11.0 kV/mm @Thickness 3.00 mm | 279 kV/in @Thickness 0.118 in | 24hr/23°C/50% RH+1hr/oil 90°C; Perpendicular; IEC 60243-1; IEC/EN 61212-2 6.1.2.1 |
| 2.40 kV/mm @Diameter >=3.00 mm | 61.0 kV/in @Diameter >=0.118 in | 24hr/23°C/50% RH+1hr/oil 90°C; Parallel; IEC 60243-1; IEC/EN 61212-2 6.1.2.1 | |
| Dissipation Factor | 0.010 @Frequency 50.0 Hz | 0.010 @Frequency 50.0 Hz | 96hr/105°C+1hr/23°C/20%RH; IEC 250; IEC/EN 61212-2 6.3 |
| 0.010 @Frequency 1000 Hz | 0.010 @Frequency 1000 Hz | 96hr/105°C+1hr/23°C/20%RH; IEC 250; IEC/EN 61212-2 6.3 | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Inert | 160 °C @Thickness 3.00 mm, Time 7.20e+7 sec | 320 °F @Thickness 0.118 in, Time 20000 hour | IEC 60695-11-10; IEC/EN 61212-2 7.1 |