- 密度 [g/cm3]: 1.28
- 弯曲强度 [MPa]: 13.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 - 1.34 g/cc | 0.0462 - 0.0484 lb/in³ | |
| Solids Content | >= 99 % | >= 99 % | |
| Viscosity | 350000 cP @Shear Rate 1.00 1/s, Temperature 23.0 °C | 350000 cP @Shear Rate 1.00 1/s, Temperature 73.4 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 13.0 MPa | 1890 psi | ISO 527-1 |
| Elongation at Break | 11 % | 11 % | ISO 527-1 |
| Modulus of Elasticity | 0.560 GPa | 81.2 ksi | ISO 527-1 |
| Adhesive Bond Strength | 13.8 MPa @Thickness 1.50 mm | 2000 psi @Thickness 0.0591 in | Lap Shear (CRS St 1203); EN 1465 |
| 15.9 MPa @Thickness 0.750 mm | 2310 psi @Thickness 0.0295 in | Lap Shear (CRS St 1203); EN 1465 | |
| Peel Strength | 3.30 kN/m | 18.8 pli | T-Peel (CRS St 1203, 0.5mm) |
| 8.00 kN/m | 45.6 pli | Impact Peel | |
| Thermal Properties | Metric | English | Comments |
| Flash Point | >= 100 °C | >= 212 °F | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 30.0 min | 0.500 hour | 180°C |