- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 0.68
- 缺口冲击强度: 0.2
- 拉伸强度 [MPa]: 42.2
- 弯曲模量 [MPa]: 1.19
- 热变形温度 [℃]: 53.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.16 g/cc @Temperature 25.0 °C | 0.0419 lb/in³ @Temperature 77.0 °F | |||
| Water Absorption | 0.68 % | 0.68 % | ASTM D570-98 | ||
| Viscosity | 350 cP @Temperature 30.0 °C | 350 cP @Temperature 86.0 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 86 - 88 | 86 - 88 | ASTM D2240 | ||
| Tensile Strength, Yield | 42.2 - 43.8 MPa | 6120 - 6350 psi | ASTM D638M | ||
| Elongation at Break | 8.0 - 16 % | 8.0 - 16 % | ASTM D638M | ||
| Tensile Modulus | 2.18 - 2.31 GPa | 316 - 335 ksi | ASTM D638M | ||
| Flexural Strength | 66.7 - 70.5 MPa | 9670 - 10200 psi | ASTM D790M | ||
| Flexural Modulus | 1.19 - 2.13 GPa | 173 - 309 ksi | ASTM D790M | ||
| Poissons Ratio | 0.43 - 0.45 | 0.43 - 0.45 | ASTM D638M | ||
| Izod Impact, Notched | 0.200 - 0.220 J/cm | 0.375 - 0.412 ft-lb/in | ASTM D256A | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 3.1 - 3.3 @Frequency 1.00e+6 Hz | 3.1 - 3.3 @Frequency 1.00e+6 Hz | ASTM D150-98 | ||
| 3.4 - 3.5 @Frequency 1000 Hz | 3.4 - 3.5 @Frequency 1000 Hz | ASTM D150-98 | |||
| 3.5 - 3.6 @Frequency 60.0 Hz | 3.5 - 3.6 @Frequency 60.0 Hz | ASTM D150-98 | |||
| Dielectric Strength | 13.2 - 14.2 kV/mm | 335 - 361 kV/in | ASTM D149-97a | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 74.6 - 75.5 µm/m-°C @Temperature -40.0 - 0.000 °C | 41.4 - 41.9 µin/in-°F @Temperature -40.0 - 32.0 °F | ASTM E831-00 | ||
| 101.2 - 110.3 µm/m-°C @Temperature 0.000 - 50.0 °C | 56.22 - 61.28 µin/in-°F @Temperature 32.0 - 122 °F | ASTM E831-00 | |||
| 114.4 - 135.8 µm/m-°C @Temperature 50.0 - 100 °C | 63.56 - 75.44 µin/in-°F @Temperature 122 - 212 °F | ASTM E831-00 | |||
| 129.5 - 138.1 µm/m-°C @Temperature 100 - 150 °C | 71.94 - 76.72 µin/in-°F @Temperature 212 - 302 °F | ASTM E831-00 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 53.0 - 56.0 °C | 127 - 133 °F | ASTM D648-98c | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 46.0 - 47.0 °C | 115 - 117 °F | ASTM D648-98c | ||
| Glass Transition Temp, Tg | 57.0 - 59.0 °C | 135 - 138 °F | ASTM E1545-00 | ||
| Descriptive Properties | |||||
| Appearance | White | ||||
| Dp (mm) | 0.11 | Slope of cure-depth vs. ln(E) curve | |||
| E10 (mJ/cm2) | 67.6 | Exposure that gives 0.254mm thickness | |||
| Ec (mJ/cm2) | 6.73 | Critical exposure | |||