- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 0.75
- 缺口冲击强度: 0.13
- 拉伸强度 [MPa]: 68.8
- 弯曲模量 [MPa]: 2.33
- 热变形温度 [℃]: 95.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.16 g/cc @Temperature 25.0 °C | 0.0419 lb/in³ @Temperature 77.0 °F | |||
| Water Absorption | 0.75 % | 0.75 % | ASTM D570-98 | ||
| Viscosity | 300 cP @Temperature 30.0 °C | 300 cP @Temperature 86.0 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 87 - 88 | 87 - 88 | ASTM D2240 | ||
| Tensile Strength, Yield | 68.8 - 69.2 MPa | 9980 - 10000 psi | ASTM D638M | ||
| Elongation at Break | 7.0 - 8.0 % | 7.0 - 8.0 % | ASTM D638M | ||
| Tensile Modulus | 2.91 - 2.99 GPa | 422 - 434 ksi | ASTM D638M | ||
| Flexural Strength | 88.5 - 91.5 MPa | 12800 - 13300 psi | ASTM D790M | ||
| Flexural Modulus | 2.33 - 2.49 GPa | 338 - 361 ksi | ASTM D790M | ||
| Poissons Ratio | 0.43 | 0.43 | ASTM D638M | ||
| Shear Modulus | 1.02 - 1.05 GPa | 148 - 152 ksi | Calculated | ||
| Izod Impact, Notched | 0.130 - 0.250 J/cm | 0.244 - 0.468 ft-lb/in | ASTM D256A | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 3.2 - 3.3 @Frequency 1.00e+6 Hz | 3.2 - 3.3 @Frequency 1.00e+6 Hz | ASTM D150-98 | ||
| 3.4 - 3.5 @Frequency 1000 Hz | 3.4 - 3.5 @Frequency 1000 Hz | ASTM D150-98 | |||
| 3.5 - 3.6 @Frequency 60.0 Hz | 3.5 - 3.6 @Frequency 60.0 Hz | ASTM D150-98 | |||
| Dielectric Strength | 15.2 - 15.7 kV/mm | 386 - 399 kV/in | ASTM D149-97a | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 63.7 - 71.8 µm/m-°C @Temperature -40.0 - 0.000 °C | 35.4 - 39.9 µin/in-°F @Temperature -40.0 - 32.0 °F | ASTM E831-00 | ||
| 75.0 - 107.5 µm/m-°C @Temperature 0.000 - 50.0 °C | 41.7 - 59.72 µin/in-°F @Temperature 32.0 - 122 °F | ASTM E831-00 | |||
| 99.4 - 111 µm/m-°C @Temperature 50.0 - 100 °C | 55.2 - 61.7 µin/in-°F @Temperature 122 - 212 °F | ASTM E831-00 | |||
| 143.4 - 173.3 µm/m-°C @Temperature 100 - 150 °C | 79.67 - 96.28 µin/in-°F @Temperature 212 - 302 °F | ASTM E831-00 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 - 97.0 °C | 203 - 207 °F | ASTM D648-98c | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 79.0 - 82.0 °C | 174 - 180 °F | ASTM D648-98c | ||
| Glass Transition Temp, Tg | 76.0 - 94.0 °C | 169 - 201 °F | ASTM E1545-00 | ||
| Descriptive Properties | |||||
| Appearance | Translucent | ||||
| Dp (mm) | 0.12 | Slope of cure-depth vs. ln(E) curve | |||
| E10 (mJ/cm2) | 57 | Exposure that gives 0.254mm thickness | |||
| Ec (mJ/cm2) | 6.38 | Critical exposure | |||