- 密度 [g/cm3]: 1.13
- 缺口冲击强度: 0.262
- 拉伸强度 [MPa]: 44.0
- 弯曲模量 [MPa]: 1.71
- 热变形温度 [℃]: 45.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc @Temperature 25.0 °C | 0.0408 lb/in³ @Temperature 77.0 °F | |||
| Viscosity | 700 cP @Temperature 30.0 °C | 700 cP @Temperature 86.0 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 81 | 81 | ASTM D2240 | ||
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | ASTM D638M | ||
| Elongation at Break | 4.7 - 7.4 % | 4.7 - 7.4 % | ASTM D638M | ||
| Modulus of Elasticity | 1.758 GPa | 255.0 ksi | ASTM D638M | ||
| Flexural Strength | 59.0 MPa | 8560 psi | ASTM D790M | ||
| Flexural Modulus | 1.71 GPa | 248 ksi | ASTM D790M | ||
| Izod Impact, Notched | 0.262 J/cm | 0.491 ft-lb/in | ASTM D256A | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 - 54.0 °C | 113 - 129 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| Appearance | Transparent Amber | ||||
| Dp (mm) | 0.14 | Slope of cure-depth vs. ln(E) curve | |||
| E10 (mJ/cm2) | 51 | Exposure that gives 0.254mm thickness | |||
| E5 (mJ/cm2) | 20 | Exposure that gives 0.127mm thickness | |||
| Ec (mJ/cm2) | 8.2 | Critical exposure | |||