- 密度 [g/cm3]: 1.85
- 吸水率 [%]: 0.2
- 缺口冲击强度: 65.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.85 g/cc | 0.0668 lb/in³ | 24hr/23°C/50% RH; ISO 1183-A; IEC/EN 60893-2 8.1 |
| Water Absorption | 0.20 % | 0.20 % | 24hr/50°C+24hr in water at 23°C,Test Specimen 50x50x3[mm]; ISO 62-1; IEC/EN 60893-2 8.2 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 320 MPa @Thickness >=1.50 mm | 46400 psi @Thickness >=0.0591 in | 24hr/23°C/50% RH; ISO 527; IEC/EN 60893-2 5.6 |
| Modulus of Elasticity | 22.0 GPa @Thickness >=1.50 mm | 3190 ksi @Thickness >=0.0591 in | 24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.2 |
| Flexural Strength | 300 MPa @Thickness >=1.50 mm | 43500 psi @Thickness >=0.0591 in | 1hr/150°C/measured at 150°C; ISO 178; IEC/EN 60893-2 5.1 |
| 450 MPa @Thickness >=1.50 mm | 65300 psi @Thickness >=0.0591 in | 24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1 | |
| 70.0 MPa @Treatment Temp. 250 °C, Time 3600 sec | 10200 psi @Treatment Temp. 482 °F, Time 1.00 hour | ISO 178; IEC/EN 60893-2 5.1 | |
| 110 MPa @Treatment Temp. 200 °C, Time 3600 sec | 16000 psi @Treatment Temp. 392 °F, Time 1.00 hour | ISO 178; IEC/EN 60893-2 5.1 | |
| 300 MPa @Treatment Temp. 150 °C, Time 3600 sec | 43500 psi @Treatment Temp. 302 °F, Time 1.00 hour | ISO 178; IEC/EN 60893-2 5.1 | |
| 380 MPa @Treatment Temp. 100 °C, Time 3600 sec | 55100 psi @Treatment Temp. 212 °F, Time 1.00 hour | ISO 178; IEC/EN 60893-2 5.1 | |
| 410 MPa @Treatment Temp. 50.0 °C, Time 3600 sec | 59500 psi @Treatment Temp. 122 °F, Time 1.00 hour | ISO 178; IEC/EN 60893-2 5.1 | |
| 450 MPa @Treatment Temp. 20.0 °C, Time 3600 sec | 65300 psi @Treatment Temp. 68.0 °F, Time 1.00 hour | ISO 178; IEC/EN 60893-2 5.1 | |
| Compressive Strength | 550 MPa @Thickness >=5.00 mm | 79800 psi @Thickness >=0.197 in | 24hr/23°C/50% RH; ISO 604; IEC/EN 60893-2 5.3 |
| 340 MPa @Treatment Temp. 250 °C, Time 3600 sec | 49300 psi @Treatment Temp. 482 °F, Time 1.00 hour | ISO 604; IEC/EN 60893-2 5.3 | |
| 360 MPa @Treatment Temp. 200 °C, Time 3600 sec | 52200 psi @Treatment Temp. 392 °F, Time 1.00 hour | ISO 604; IEC/EN 60893-2 5.3 | |
| 400 MPa @Treatment Temp. 150 °C, Time 3600 sec | 58000 psi @Treatment Temp. 302 °F, Time 1.00 hour | ISO 604; IEC/EN 60893-2 5.3 | |
| 450 MPa @Treatment Temp. 100 °C, Time 3600 sec | 65300 psi @Treatment Temp. 212 °F, Time 1.00 hour | ISO 604; IEC/EN 60893-2 5.3 | |
| 530 MPa @Treatment Temp. 50.0 °C, Time 3600 sec | 76900 psi @Treatment Temp. 122 °F, Time 1.00 hour | ISO 604; IEC/EN 60893-2 5.3 | |
| 570 MPa @Treatment Temp. 20.0 °C, Time 3600 sec | 82700 psi @Treatment Temp. 68.0 °F, Time 1.00 hour | ISO 604; IEC/EN 60893-2 5.3 | |
| Shear Strength | 55.0 MPa @Thickness >=5.00 mm | 7980 psi @Thickness >=0.197 in | 24hr/23°C/50% RH; IEC/EN 60893-2 5.5 |
| Izod Impact, Notched (ISO) | 65.0 kJ/m² @Thickness >=5.00 mm | 30.9 ft-lb/in² @Thickness >=0.197 in | 24hr/23°C/50% RH; ISO 180/2A; IEC/EN 60893-2 5.4.3 |
| Electrical Properties | Metric | English | Comments |
| Insulation Resistance | 5.00e+11 ohm @Thickness >=3.00 mm | 5.00e+11 ohm @Thickness >=0.118 in | 24hr/50°C+24h in water at 23°C; IEC 60167; IEC/EN 60893-2 6.3 |
| Dielectric Constant | 5.0 @Thickness <=3.00 mm, Frequency 50.0 Hz | 5.0 @Thickness <=0.118 in, Frequency 50.0 Hz | 96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2 |
| 5.0 @Thickness <=3.00 mm, Frequency 1.00e+6 Hz | 5.0 @Thickness <=0.118 in, Frequency 1.00e+6 Hz | 96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2 | |
| Dielectric Strength | 2.80 kV/mm @Thickness >=3.00 mm | 71.1 kV/in @Thickness >=0.118 in | 24hr/23°C/50% RH+1hr/oil 90°C; Parallel; IEC 60245-1; IEC/EN 60893-2 6.1.3.2 |
| 18.0 kV/mm @Thickness 3.00 mm | 457 kV/in @Thickness 0.118 in | 24hr/23°C/50% RH+1hr/oil 90°C; Perpendicular; IEC 60245-1; IEC/EN 60893-2 6.1.3.1 | |
| Dissipation Factor | 0.0080 @Frequency 50.0 Hz | 0.0080 @Frequency 50.0 Hz | 96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2 |
| 0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | 96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2 | |
| Comparative Tracking Index | 200 V @Thickness 3.00 mm | 200 V @Thickness 0.118 in | IEC 60112; IEC/EN 60893-2 6.4 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Inert | 180 °C @Thickness 0.000 mm, Time 7.20e+7 sec | 356 °F @Thickness 0.000 in, Time 20000 hour | IEC 60216; IEC/EN 60893-2 7.1 |