- 吸水率 [%]: 0.1
- 缺口冲击强度: 0.246
- 弯曲模量 [MPa]: 3.79
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Water Absorption | 0.10 % | 0.10 % | Percent weight gain after 24 hours immersion at 25°C | ||
| 0.10 % | 0.10 % | Percent weight loss after 24 hours at 150°C | |||
| Viscosity | 10000 cP | 10000 cP | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 90 | 90 | |||
| Tensile Strength at Break | 75.8 MPa | 11000 psi | |||
| Elongation at Break | 3.8 % | 3.8 % | |||
| Flexural Strength | 131 MPa | 19000 psi | |||
| Flexural Modulus | 3.79 GPa | 550 ksi | Initial flexural modulus | ||
| Compressive Yield Strength | 111 MPa | 16100 psi | |||
| Izod Impact, Notched | 0.246 J/cm | 0.460 ft-lb/in | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 6.00e+10 ohm-cm @Temperature 130 °C | 6.00e+10 ohm-cm @Temperature 266 °F | |||
| 8.00e+12 ohm-cm @Temperature 93.0 °C | 8.00e+12 ohm-cm @Temperature 199 °F | ||||
| 1.00e+15 ohm-cm @Temperature 66.0 °C | 1.00e+15 ohm-cm @Temperature 151 °F | ||||
| 2.80e+16 ohm-cm @Temperature 25.0 °C | 2.80e+16 ohm-cm @Temperature 77.0 °F | ||||
| Dielectric Constant | 4.19 | 4.19 | |||
| Dissipation Factor | 0.026 @Frequency 1e+7 Hz | 0.026 @Frequency 1e+7 Hz | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 99.0 °C | 210 °F | Deflection Temp; Load not specified | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 240 - 480 min | 4.00 - 8.00 hour | Mixture reaches handling strength in 4 to 8 hours. | ||
| 5760 - 10080 min | 96.0 - 168.0 hour | For full cure. Maximum high temperature properties are obtained with a post cure of about 2 hours at 93°C to 121°C. | |||
| Pot Life | 15 min | 15 min | Value for 0.25 lb at 25°C | ||
| Descriptive Properties | |||||
| Maximum Exotherm | >204°C | 25 grams, 1 inch thick, at ambient temperature of 25°C and a gel time of 15 minutes. | |||
| Mix Ratio | 100:20 | Resin:Hardener by Weight | |||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.