| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Storage Temperature | 25.0 °C | 77.0 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 34.5 MPa | 5000 psi | |||
| Elongation at Break | 9.0 % | 9.0 % | |||
| Tensile Modulus | 2.28 GPa | 331 ksi | |||
| Compressive Strength | 60.7 MPa | 8800 psi | |||
| Compressive Modulus | 1.82 GPa | 264 ksi | |||
| Adhesive Bond Strength | 6.90 MPa @Temperature 93.0 °C | 1000 psi @Temperature 199 °F | Tensile Lap Shear | ||
| 23.5 MPa @Temperature -55.0 °C | 3410 psi @Temperature -67.0 °F | Tensile Lap Shear | |||
| 31.7 MPa @Temperature 25.0 °C | 4600 psi @Temperature 77.0 °F | Tensile Lap Shear | |||
| Peel Strength | 6.00 kN/m | 34.2 pli | Bell Peel | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | >= 82.0 °C | >= 180 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 min @Temperature 82.0 °C | 1.00 hour @Temperature 180 °F | |||
| 7200 - 10100 min @Temperature 25.0 °C | 120 - 168 hour @Temperature 77.0 °F | ||||
| Pot Life | 25 min | 25 min | |||
| Descriptive Properties | |||||
| Consistency | Moderate Viscosity | ||||
| Form | 2 parts | ||||
| Mix Ratio, Part A:Part B | 100:19 | ||||
| Peel Strength | Moderate | ||||