| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Storage Temperature | 4.00 °C | 39.2 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 56.6 MPa | 8210 psi | |||
| Elongation at Break | 2.5 % | 2.5 % | |||
| Tensile Modulus | 2.90 GPa | 421 ksi | |||
| Compressive Strength | 36.6 MPa | 5310 psi | compressive shear strength as a wet lay-up resin with 3K-70-P fiber | ||
| Adhesive Bond Strength | 15.2 MPa @Temperature -55.0 °C | 2200 psi @Temperature -67.0 °F | Tensile Lap Shear | ||
| 20.7 MPa @Temperature 93.0 °C | 3000 psi @Temperature 199 °F | Tensile Lap Shear | |||
| 24.1 MPa @Temperature 25.0 °C | 3500 psi @Temperature 77.0 °F | Tensile Lap Shear | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | >= 177 °C | >= 351 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 210 min @Temperature 93.0 °C | 3.50 hour @Temperature 199 °F | |||
| Pot Life | 120 min | 120 min | |||
| Descriptive Properties | |||||
| Consistency | Low Viscosity | ||||
| Form | 2 parts | ||||
| Mix Ratio, Part A:Part B | 100:56 | ||||
| Peel Strength | Nil | ||||