| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Storage Temperature | 4.00 °C | 39.2 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 24.1 MPa | 3500 psi | |||
| Elongation at Break | 9.0 % | 9.0 % | |||
| Tensile Modulus | 2.60 GPa | 377 ksi | |||
| Compressive Strength | 73.8 MPa | 10700 psi | |||
| Compressive Modulus | 1.77 GPa | 257 ksi | |||
| Adhesive Bond Strength | 7.60 MPa @Temperature 93.0 °C | 1100 psi @Temperature 199 °F | Tensile Lap Shear | ||
| 19.3 MPa @Temperature -55.0 °C | 2800 psi @Temperature -67.0 °F | Tensile Lap Shear | |||
| 29.0 MPa @Temperature 25.0 °C | 4210 psi @Temperature 77.0 °F | Tensile Lap Shear | |||
| Peel Strength | 0.800 kN/m | 4.56 pli | Bell Peel | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 121 °C | 250 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 min @Temperature 82.0 °C | 1.00 hour @Temperature 180 °F | |||
| 7200 - 10100 min @Temperature 25.0 °C | 120 - 168 hour @Temperature 77.0 °F | ||||
| Pot Life | 30 min | 30 min | |||
| Descriptive Properties | |||||
| Consistency | Low Viscosity | ||||
| Form | 2 parts | ||||
| Mix Ratio, Part A:Part B | 100:45 | ||||
| Peel Strength | Low | ||||