- 密度 [g/cm3]: 1.6
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 600 MPa | 87000 psi | Longitudinal | ||
| 600 MPa | 87000 psi | Transverse | |||
| Elongation at Break | 0.80 % | 0.80 % | Longitudinal Compressive Strain | ||
| 0.80 % | 0.80 % | Transverse Compressive Strain | |||
| 0.85 % | 0.85 % | Longitudinal - Tensile | |||
| 0.85 % | 0.85 % | Transverse - Tensile | |||
| 1.8 % | 1.8 % | Shear - In Plane | |||
| Modulus of Elasticity | 70.0 GPa | 10200 ksi | Transverse | ||
| Tensile Modulus | 70.0 GPa | 10200 ksi | Longitudinal | ||
| Compressive Strength | 570 MPa | 82700 psi | Longitudinal | ||
| 570 MPa | 82700 psi | Transverse | |||
| Shear Modulus | 5.00 GPa | 725 ksi | In Plane | ||
| Shear Strength | 90.0 MPa | 13100 psi | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 2.10 µm/m-°C @Temperature 20.0 °C | 1.17 µin/in-°F @Temperature 68.0 °F | Longitudinal | ||
| CTE, linear, Transverse to Flow | 2.10 µm/m-°C @Temperature 20.0 °C | 1.17 µin/in-°F @Temperature 68.0 °F | |||
| Descriptive Properties | |||||
| Volume Fraction Fibers, % | 50 | ||||