- 密度 [g/cm3]: 1.6
- 弯曲模量 [MPa]: 125
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 50.0 MPa | 7250 psi | Transverse | ||
| 1100 - 1900 MPa | 160000 - 276000 psi | Longitudinal | |||
| Elongation at Break | 0.50 % | 0.50 % | Transverse - Tensile | ||
| 0.80 % | 0.80 % | Longitudinal Compressive Strain | |||
| 1.1 % | 1.1 % | Longitudinal - Tensile | |||
| 2.5 % | 2.5 % | Transverse Compressive Strain | |||
| Modulus of Elasticity | 10.0 GPa | 1450 ksi | Transverse | ||
| Tensile Modulus | 120 - 140 GPa | 17400 - 20300 ksi | Longitudinal | ||
| Flexural Strength | 1200 MPa | 174000 psi | Longitudinal | ||
| Flexural Modulus | 125 GPa | 18100 ksi | Longitudinal | ||
| Compressive Strength | 50.0 - 250 MPa | 7250 - 36300 psi | Transverse | ||
| 800 - 1300 MPa | 116000 - 189000 psi | Longitudinal | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | -0.700 - -0.300 µm/m-°C @Temperature 20.0 °C | -0.389 - -0.167 µin/in-°F @Temperature 68.0 °F | Longitudinal | ||
| CTE, linear, Transverse to Flow | 28.0 µm/m-°C @Temperature 20.0 °C | 15.6 µin/in-°F @Temperature 68.0 °F | |||
| Descriptive Properties | |||||
| Volume Fraction Fibers, % | 55-60 | ||||