- 拉伸强度 [MPa]: 2170.0
- 断裂伸长率 [%]: 1700
- 弯曲模量 [MPa]: 123
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 2170 MPa @Temperature 25.0 °C | 315000 psi @Temperature 77.0 °F | 0°, Dry |
| Elongation at Yield | 1.4 % | 1.4 % | 0°, Dry |
| Tensile Modulus | 145 GPa | 21000 ksi | 0°, Dry |
| Flexural Yield Strength | 1700 MPa @Temperature 25.0 °C | 247000 psi @Temperature 77.0 °F | 0°, Dry |
| Flexural Modulus | 123 GPa @Temperature 25.0 °C | 17800 ksi @Temperature 77.0 °F | 0°, Dry |
| Compressive Yield Strength | 262 MPa @Temperature 82.0 °C | 38000 psi @Temperature 180 °F | Open hole compression, Wet |
| 303 MPa @Temperature 25.0 °C | 43900 psi @Temperature 77.0 °F | After 1500 in-inlb/in impact, Dry | |
| 303 MPa @Temperature 25.0 °C | 43900 psi @Temperature 77.0 °F | Open hole compression, Dry | |
| 1170 MPa @Temperature 82.0 °C | 170000 psi @Temperature 180 °F | 0°, Wet | |
| 1240 MPa @Temperature 121 °C | 180000 psi @Temperature 250 °F | 0°, Dry | |
| 1410 MPa @Temperature 82.0 °C | 205000 psi @Temperature 180 °F | 0°, Dry | |
| 1590 MPa @Temperature 25.0 °C | 231000 psi @Temperature 77.0 °F | 0°, Dry | |
| Compressive Modulus | 123 GPa @Temperature 82.0 °C | 17800 ksi @Temperature 180 °F | 0°, Wet |
| 127 GPa @Temperature 121 °C | 18400 ksi @Temperature 250 °F | 0°, Dry | |
| 129 GPa @Temperature 104 °C | 18700 ksi @Temperature 219 °F | 0°, Wet | |
| 138 GPa @Temperature 25.0 °C | 20000 ksi @Temperature 77.0 °F | 0°, Dry | |
| Shear Strength | 50.3 MPa @Temperature 121 °C | 7300 psi @Temperature 250 °F | Short Beam, Wet |
| 65.5 MPa @Temperature 121 °C | 9500 psi @Temperature 250 °F | Short Beam, Dry | |
| 82.7 MPa @Temperature 82.0 °C | 12000 psi @Temperature 180 °F | Short Beam, Wet | |
| 84.8 MPa @Temperature 82.0 °C | 12300 psi @Temperature 180 °F | Short Beam, Dry | |
| 107 MPa @Temperature 25.0 °C | 15500 psi @Temperature 77.0 °F | Short Beam, Dry | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 93.3 °C | 200 °F | Epoxy Matrix Limit |