- 拉伸强度 [MPa]: 627.0
- 断裂伸长率 [%]: 848
- 弯曲模量 [MPa]: 28.3
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 627 MPa @Temperature 23.0 °C | 90900 psi @Temperature 73.4 °F | 0° |
| Elongation at Yield | 2.8 % | 2.8 % | 0°, Room Temperature |
| Tensile Modulus | 28.3 GPa @Temperature 23.0 °C | 4100 ksi @Temperature 73.4 °F | 0° |
| Flexural Yield Strength | 848 MPa | 123000 psi | 0°, Room Temperature |
| Flexural Modulus | 28.3 GPa | 4100 ksi | 0°, Room Temperature |
| Compressive Yield Strength | 586 MPa | 85000 psi | 0°, Room Temperature |
| 317 MPa @Temperature 163 °C | 46000 psi @Temperature 325 °F | 0°, Wet | |
| 345 MPa @Temperature 149 °C | 50000 psi @Temperature 300 °F | 0°, Wet | |
| 365 MPa @Temperature 204 °C | 52900 psi @Temperature 399 °F | 0° | |
| 379 MPa @Temperature 191 °C | 55000 psi @Temperature 376 °F | 0° | |
| 427 MPa @Temperature 177 °C | 61900 psi @Temperature 351 °F | 0° | |
| 434 MPa @Temperature 163 °C | 62900 psi @Temperature 325 °F | 0° | |
| Compressive Modulus | 29.6 GPa | 4290 ksi | 0°, Room Temperature |
| 29.0 GPa @Temperature 191 °C | 4210 ksi @Temperature 376 °F | 0° | |
| 29.6 GPa @Temperature 163 °C | 4290 ksi @Temperature 325 °F | 0° | |
| 29.6 GPa @Temperature 204 °C | 4290 ksi @Temperature 399 °F | 0° | |
| 31.0 GPa @Temperature 177 °C | 4500 ksi @Temperature 351 °F | 0° | |
| Shear Strength | 75.2 MPa | 10900 psi | Short Beam; Room Temperature |
| 35.2 MPa @Temperature 163 °C | 5110 psi @Temperature 325 °F | Short Beam, Wet | |
| 37.2 MPa @Temperature 204 °C | 5400 psi @Temperature 399 °F | Short Beam | |
| 37.2 MPa @Temperature 149 °C | 5400 psi @Temperature 300 °F | Short Beam, Wet | |
| 41.4 MPa @Temperature 177 °C | 6000 psi @Temperature 351 °F | Short Beam | |
| 43.4 MPa @Temperature 191 °C | 6290 psi @Temperature 376 °F | Short Beam | |
| 52.4 MPa @Temperature 163 °C | 7600 psi @Temperature 325 °F | Short Beam | |