- 密度 [g/cm3]: 0.66
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.660 g/cc | 0.0238 lb/in³ | |
| Density | 0.660 g/cc | 0.0238 lb/in³ | |
| Thickness | 127 microns | 5.00 mil | Nominal |
| 135 microns | 5.30 mil | Typical; ASTM D374 | |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 7.8 % | 7.8 % | ASTM D828 |
| Film Elongation at Break, TD | 8.9 % | 8.9 % | ASTM D828 |
| Tear Strength, Total | 13.0 N | 2.92 lb (f) | Initial in TD; ASTM D1004 |
| 25.0 N | 5.62 lb (f) | Initial in MD; ASTM D1004 | |
| Film Tensile Strength at Break, MD | 48.3 MPa | 7010 psi | Calculated from mfr's report of 65 N/cm per ASTM D828 and the typical thickness |
| Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | Calculated from mfr's report of 31 N/cm per ASTM D828 and the typical thickness |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 1.7 @Frequency 60 Hz | 1.7 @Frequency 60 Hz | ASTM D150 |
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | AC Rapid Rise; ASTM D149 |
| 37.4 kV/mm | 950 kV/in | Full-wave Impulse; ASTM D3426 | |
| Dissipation Factor | 0.0050 @Frequency 60 Hz | 0.0050 @Frequency 60 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.0830 W/m-K @Temperature 150 °C | 0.576 BTU-in/hr-ft²-°F @Temperature 302 °F | measured on 10 mil sample |
| Maximum Service Temperature, Air | 220 °C | 428 °F | 220°C insulation by UL |
| Oxygen Index | 29 % | 29 % | ASTM D2863 |